EN 10222-5 Grade X6CrNiTiB18-10 solution annealed (+AT)
EN 10222-5 Grade X6CrNiTiB18-10 solution annealed (+AT) introduction
Steel X6CrNiTiB18-10 (1.4941) is a high temperature steel for application in pressure vessel and steam boiler construction as well as in nuclear power plant construction.
Equivalent material: IS X04Cr18Ni10Ti, JIS SUSF321, KS STSF321, ASTM A965 Grade F321, UNS S32100, ASTM Grade F321, ASTM F321, DIN X8CrNiTi18-10, DIN 1.4941, DIN X6CrNiTiB18-10, DIN X7CrNiTiB18-10, AFNOR Z6CNT18-10, AISI 321H, SAE 321H, EN X7CrNiTiB18-10, EN 1.4941, UNS S32109
EN 10222-5 Grade X6CrNiTiB18-10 solution annealed (+AT) general
| Property | Temperature | Value |
|---|---|---|
| Density | 20.0 °C | Density of 7.9 - 7.93 g/cm³ |
EN 10222-5 Grade X6CrNiTiB18-10 solution annealed (+AT) thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Coefficient of thermal expansion | -100.0 °C | Coefficient of thermal expansion of 1.49E-5 1/K | - |
| - | 20.0 °C | Coefficient of thermal expansion of 1.61E-5 1/K | - |
| - | 100.0 °C | Coefficient of thermal expansion of 1.67E-5 1/K | - |
| - | 200.0 °C | Coefficient of thermal expansion of 1.72E-5 1/K | - |
| - | 300.0 °C | Coefficient of thermal expansion of 1.77E-5 1/K | - |
| - | 400.0 °C | Coefficient of thermal expansion of 1.81E-5 1/K | - |
| - | 500.0 °C | Coefficient of thermal expansion of 1.84E-5 1/K | - |
| - | 600.0 °C | Coefficient of thermal expansion of 1.88E-5 1/K | - |
| - | 700.0 °C | Coefficient of thermal expansion of 1.91E-5 1/K | - |
| - | 800.0 °C | Coefficient of thermal expansion of 1.94E-5 1/K | - |
| - | 900.0 °C | Coefficient of thermal expansion of 1.97E-5 1/K | - |
| - | 1000.0 °C | Coefficient of thermal expansion of 2E-5 1/K | - |
| Melting point | - | Melting point of 1230 - 1480 °C | Typical for Austenitic Stainless Steel |
| Specific heat capacity | -100.0 °C | Specific heat capacity of 440 J/(kg·K) | - |
| - | 20.0 °C | Specific heat capacity of 450 - 472 J/(kg·K) | - |
| - | 100.0 °C | Specific heat capacity of 487 J/(kg·K) | - |
| - | 200.0 °C | Specific heat capacity of 503 J/(kg·K) | - |
| - | 300.0 °C | Specific heat capacity of 512 J/(kg·K) | - |
| - | 400.0 °C | Specific heat capacity of 520 J/(kg·K) | - |
| - | 500.0 °C | Specific heat capacity of 530 J/(kg·K) | - |
| - | 600.0 °C | Specific heat capacity of 541 J/(kg·K) | - |
| - | 700.0 °C | Specific heat capacity of 551 J/(kg·K) | - |
| - | 800.0 °C | Specific heat capacity of 559 J/(kg·K) | - |
| - | 900.0 °C | Specific heat capacity of 565 J/(kg·K) | - |
| - | 1000.0 °C | Specific heat capacity of 571 J/(kg·K) | - |
| Thermal conductivity | 20.0 °C | Thermal conductivity of 14.3 - 17 W/(m·K) | - |
| - | 100.0 °C | Thermal conductivity of 15.8 W/(m·K) | - |
| - | 200.0 °C | Thermal conductivity of 17.5 W/(m·K) | - |
| - | 300.0 °C | Thermal conductivity of 19 W/(m·K) | - |
| - | 400.0 °C | Thermal conductivity of 20.5 W/(m·K) | - |
| - | 500.0 °C | Thermal conductivity of 21.9 W/(m·K) | - |
| - | 600.0 °C | Thermal conductivity of 23.3 W/(m·K) | - |
| - | 700.0 °C | Thermal conductivity of 24.6 W/(m·K) | - |
| - | 800.0 °C | Thermal conductivity of 26 W/(m·K) | - |
| - | 900.0 °C | Thermal conductivity of 27.4 W/(m·K) | - |
| - | 1000.0 °C | Thermal conductivity of 28.8 W/(m·K) | - |
| Thermal diffusivity | 20.0 °C | Thermal diffusivity of 3.8 mm²/s | - |
| - | 100.0 °C | Thermal diffusivity of 4 mm²/s | - |
| - | 200.0 °C | Thermal diffusivity of 4.2 mm²/s | - |
| - | 300.0 °C | Thermal diffusivity of 4.6 mm²/s | - |
| - | 400.0 °C | Thermal diffusivity of 4.8 mm²/s | - |
| - | 500.0 °C | Thermal diffusivity of 4.9 mm²/s | - |
| - | 600.0 °C | Thermal diffusivity of 5 mm²/s | - |
| - | 700.0 °C | Thermal diffusivity of 5.3 mm²/s | - |
| - | 800.0 °C | Thermal diffusivity of 5.6 mm²/s | - |
| - | 900.0 °C | Thermal diffusivity of 5.9 mm²/s | - |
| - | 1000.0 °C | Thermal diffusivity of 6 mm²/s | - |
EN 10222-5 Grade X6CrNiTiB18-10 solution annealed (+AT) chemical
| Property | Value |
|---|---|
| Boron | Boron of 1.5E-3 - 5E-3 % |
| Carbon | Carbon of 0.04 - 0.08 % |
| Chromium | Chromium of 17 - 19 % |
| Manganese | Manganese of 2 % |
| Nickel | Nickel of 9 - 12 % |
| Phosphorus | Phosphorus of 0.04 % |
| Silicon | Silicon of 1 % |
| Sulfur | Sulfur of 0.015 % |
| Titanium | Titanium of 0.8 % |
EN 10222-5 Grade X6CrNiTiB18-10 solution annealed (+AT) electrical
| Property | Temperature | Value |
|---|---|---|
| Electrical resistivity | 20.0 °C | Electrical resistivity of 7.1E-7 Ω·m |
| - | 100.0 °C | Electrical resistivity of 7.76E-7 Ω·m |
| - | 200.0 °C | Electrical resistivity of 8.49E-7 Ω·m |
| - | 300.0 °C | Electrical resistivity of 9.14E-7 Ω·m |
| - | 400.0 °C | Electrical resistivity of 9.71E-7 Ω·m |
| - | 500.0 °C | Electrical resistivity of 1.02E-6 Ω·m |
| - | 600.0 °C | Electrical resistivity of 1.07E-6 Ω·m |
| - | 700.0 °C | Electrical resistivity of 1.1E-6 Ω·m |
| - | 800.0 °C | Electrical resistivity of 1.14E-6 Ω·m |
| - | 900.0 °C | Electrical resistivity of 1.17E-6 Ω·m |
| - | 1000.0 °C | Electrical resistivity of 1.19E-6 Ω·m |
EN 10222-5 Grade X6CrNiTiB18-10 solution annealed (+AT) mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | -100.0 °C | Elastic modulus of 206 GPa | - |
| - | 20.0 °C | Elastic modulus of 196 - 200 GPa | - |
| - | 100.0 °C | Elastic modulus of 190 GPa | - |
| - | 200.0 °C | Elastic modulus of 182 GPa | - |
| - | 300.0 °C | Elastic modulus of 174 GPa | - |
| - | 400.0 °C | Elastic modulus of 166 GPa | - |
| - | 500.0 °C | Elastic modulus of 158 GPa | - |
| - | 600.0 °C | Elastic modulus of 150 GPa | - |
| - | 700.0 °C | Elastic modulus of 142 GPa | - |
| - | 800.0 °C | Elastic modulus of 134 GPa | - |
| - | 900.0 °C | Elastic modulus of 127 GPa | - |
| - | 1000.0 °C | Elastic modulus of 120 GPa | - |
| Elongation | 20.0 °C | Elongation of 30 - 40 % | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.3 [-] | Typical for Austenitic Stainless Steel |
| Shear modulus | 23.0 °C | Shear modulus of 77 GPa | Typical for Austenitic Stainless Steel |
| Tensile strength | 20.0 °C | Tensile strength of 490 - 690 MPa | - |
| Yield strength Rp0.2 | 20.0 °C | Yield strength Rp0.2 of 175 MPa | - |
| Yield strength Rp1.0 | 20.0 °C | Yield strength Rp1.0 of 210 MPa | - |
Unlock the potential of your projects and drive success with our high-performance steel.
-- Our promise
Similar or equivalent steel materials
- Sandvik 6R35
- DIN 17440 Grade X6CrNiTi18-10 solution heat-treated and quenched
- DIN 17440 Grade X6CrNiTi18-10 quenched (+Q)
- EN 10028-7 Grade X6CrNiTiB18-10 solution annealed (+AT)
- EN 10216-5 Grade X8CrNiTi18-10 solution annealed (+AT)
- EN 10216-5 Grade X7CrNiTiB18-10 solution annealed (+AT)
- EN 10250-4 Grade X6CrNiTi18-10 solution annealed (+AT)
- EN 10222-5 Grade X6CrNiTi18-10 solution annealed (+AT)
- DIN 17460 Grade X8CrNiTi18-10 solution annealed (+AT)
- EN 10088-1 Grade X6CrNiTi18-10 strain-hardened (+C700)