DIN 17440 Grade X6CrNiTi18-10 solution heat-treated and quenched
DIN 17440 Grade X6CrNiTi18-10 solution heat-treated and quenched introduction
Properties:
- is the with titanium stabilised variant of 1.4301
- thus after welding also with material thicknesses > 6 mm resistant to intergranular corrosion
- due to the Ti-additive the steel is not high polishable
- is certified for the construction of pressure tanks to 300 °C, if no disintegration of grains-releasing media are present, then up to 550°C is possible
- the strength grades E 225, E 355 are usual.
Application:
- employment in large extent for welded parts in the chemical apparatus engineering
- food, luxuries, fat and soap industry
- in the film and photo industry, in leather and sugar factories and for houseware
- in architecure for construction units with supporting function is certified (extended licence notice No. Z-30.44.1 of Institut für Bautechnik Berlin from 1 February 1994)
Equivalent material: AS 321, AFNOR Z6CNT18-10, BS 321S31, GOST 12Ch18N10T, ISO 15, UNI X6CrNiTi18-11, JIS SUS321, NS 14355, ÖNORM X6CrNiTi18-10S, PN 0H18N10T, SS 2337, UNE F.3523, UNE X6CrNiTi18-11, ASTM 321, DIN 1.4541, DIN X10CrNiMoTi18-10, BS 321S12, BS 321S51, UNI X6CrNiTi1811, UNE F.3553, AISI 321, SAE 321, JIS SUS321TPY, JIS SUS321TP, JIS SUS321TF, JIS SUS321TB, EN X6CrNiTi18-10, EN 1.4541, GOST 06Ch18N10T, GOST 08X18H10T, GOST 12X18H10T, GB 0Cr18Ni11Ti, UNS S32100, IS X04Cr18Ni10Ti
DIN 17440 Grade X6CrNiTi18-10 solution heat-treated and quenched general
| Property | Temperature | Value |
|---|---|---|
| Density | 20.0 °C | Density of 7.9 - 7.93 g/cm³ |
DIN 17440 Grade X6CrNiTi18-10 solution heat-treated and quenched thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Coefficient of thermal expansion | -100.0 °C | Coefficient of thermal expansion of 1.49E-5 1/K | - |
| - | 20.0 °C | Coefficient of thermal expansion of 1.61E-5 1/K | - |
| - | 100.0 °C | Coefficient of thermal expansion of 1.6E-5 - 1.67E-5 1/K | - |
| - | 200.0 °C | Coefficient of thermal expansion of 1.65E-5 - 1.72E-5 1/K | - |
| - | 300.0 °C | Coefficient of thermal expansion of 1.7E-5 - 1.77E-5 1/K | - |
| - | 400.0 °C | Coefficient of thermal expansion of 1.75E-5 - 1.81E-5 1/K | - |
| - | 500.0 °C | Coefficient of thermal expansion of 1.8E-5 - 1.84E-5 1/K | - |
| - | 600.0 °C | Coefficient of thermal expansion of 1.88E-5 1/K | - |
| - | 700.0 °C | Coefficient of thermal expansion of 1.91E-5 1/K | - |
| - | 800.0 °C | Coefficient of thermal expansion of 1.94E-5 1/K | - |
| - | 900.0 °C | Coefficient of thermal expansion of 1.97E-5 1/K | - |
| - | 1000.0 °C | Coefficient of thermal expansion of 2E-5 1/K | - |
| Max service temperature, long | - | Max service temperature, long of 0 - 550 °C | - |
| Melting point | - | Melting point of 1230 - 1480 °C | Typical for Austenitic Stainless Steel |
| Specific heat capacity | -100.0 °C | Specific heat capacity of 440 J/(kg·K) | - |
| - | 20.0 °C | Specific heat capacity of 472 - 500 J/(kg·K) | - |
| - | 100.0 °C | Specific heat capacity of 487 J/(kg·K) | - |
| - | 200.0 °C | Specific heat capacity of 503 J/(kg·K) | - |
| - | 300.0 °C | Specific heat capacity of 512 J/(kg·K) | - |
| - | 400.0 °C | Specific heat capacity of 520 J/(kg·K) | - |
| - | 500.0 °C | Specific heat capacity of 530 J/(kg·K) | - |
| - | 600.0 °C | Specific heat capacity of 541 J/(kg·K) | - |
| - | 700.0 °C | Specific heat capacity of 551 J/(kg·K) | - |
| - | 800.0 °C | Specific heat capacity of 559 J/(kg·K) | - |
| - | 900.0 °C | Specific heat capacity of 565 J/(kg·K) | - |
| - | 1000.0 °C | Specific heat capacity of 571 J/(kg·K) | - |
| Thermal conductivity | 20.0 °C | Thermal conductivity of 14.3 - 15 W/(m·K) | - |
| - | 100.0 °C | Thermal conductivity of 15.8 W/(m·K) | - |
| - | 200.0 °C | Thermal conductivity of 17.5 W/(m·K) | - |
| - | 300.0 °C | Thermal conductivity of 19 W/(m·K) | - |
| - | 400.0 °C | Thermal conductivity of 20.5 W/(m·K) | - |
| - | 500.0 °C | Thermal conductivity of 21.9 W/(m·K) | - |
| - | 600.0 °C | Thermal conductivity of 23.3 W/(m·K) | - |
| - | 700.0 °C | Thermal conductivity of 24.6 W/(m·K) | - |
| - | 800.0 °C | Thermal conductivity of 26 W/(m·K) | - |
| - | 900.0 °C | Thermal conductivity of 27.4 W/(m·K) | - |
| - | 1000.0 °C | Thermal conductivity of 28.8 W/(m·K) | - |
| Thermal diffusivity | 20.0 °C | Thermal diffusivity of 3.8 mm²/s | - |
| - | 100.0 °C | Thermal diffusivity of 4 mm²/s | - |
| - | 200.0 °C | Thermal diffusivity of 4.2 mm²/s | - |
| - | 300.0 °C | Thermal diffusivity of 4.6 mm²/s | - |
| - | 400.0 °C | Thermal diffusivity of 4.8 mm²/s | - |
| - | 500.0 °C | Thermal diffusivity of 4.9 mm²/s | - |
| - | 600.0 °C | Thermal diffusivity of 5 mm²/s | - |
| - | 700.0 °C | Thermal diffusivity of 5.3 mm²/s | - |
| - | 800.0 °C | Thermal diffusivity of 5.6 mm²/s | - |
| - | 900.0 °C | Thermal diffusivity of 5.9 mm²/s | - |
| - | 1000.0 °C | Thermal diffusivity of 6 mm²/s | - |
DIN 17440 Grade X6CrNiTi18-10 solution heat-treated and quenched chemical
| Property | Value |
|---|---|
| Carbon | Carbon of 0.08 % |
| Chromium | Chromium of 17 - 19 % |
| Manganese | Manganese of 2 % |
| Nickel | Nickel of 9 - 12 % |
| Phosphorus | Phosphorus of 0.05 - 0.45 % |
| Silicon | Silicon of 1 % |
| Sulfur | Sulfur of 0.015 - 0.03 % |
| Titanium | Titanium of 0.7 - 0.8 % |
DIN 17440 Grade X6CrNiTi18-10 solution heat-treated and quenched electrical
| Property | Temperature | Value |
|---|---|---|
| Electrical resistivity | 20.0 °C | Electrical resistivity of 7.1E-7 - 7.3E-7 Ω·m |
| - | 100.0 °C | Electrical resistivity of 7.76E-7 Ω·m |
| - | 200.0 °C | Electrical resistivity of 8.49E-7 Ω·m |
| - | 300.0 °C | Electrical resistivity of 9.14E-7 Ω·m |
| - | 400.0 °C | Electrical resistivity of 9.71E-7 Ω·m |
| - | 500.0 °C | Electrical resistivity of 1.02E-6 Ω·m |
| - | 600.0 °C | Electrical resistivity of 1.07E-6 Ω·m |
| - | 700.0 °C | Electrical resistivity of 1.1E-6 Ω·m |
| - | 800.0 °C | Electrical resistivity of 1.14E-6 Ω·m |
| - | 900.0 °C | Electrical resistivity of 1.17E-6 Ω·m |
| - | 1000.0 °C | Electrical resistivity of 1.19E-6 Ω·m |
DIN 17440 Grade X6CrNiTi18-10 solution heat-treated and quenched mechanical
| Property | Temperature | Value |
|---|---|---|
| Elastic modulus | -100.0 °C | Elastic modulus of 206 GPa |
| - | 20.0 °C | Elastic modulus of 196 - 200 GPa |
| - | 95.0 °C | Elastic modulus of 193.05 GPa |
| - | 100.0 °C | Elastic modulus of 190 - 194 GPa |
| - | 150.0 °C | Elastic modulus of 188.23 GPa |
| - | 200.0 °C | Elastic modulus of 182 - 186 GPa |
| - | 205.0 °C | Elastic modulus of 182.71 GPa |
| - | 260.0 °C | Elastic modulus of 177.88 GPa |
| - | 300.0 °C | Elastic modulus of 174 - 179 GPa |
| - | 315.0 °C | Elastic modulus of 174.44 GPa |
| - | 370.0 °C | Elastic modulus of 168.92 GPa |
| - | 400.0 °C | Elastic modulus of 166 - 172 GPa |
| - | 425.0 °C | Elastic modulus of 164.1 GPa |
| - | 485.0 °C | Elastic modulus of 159.96 GPa |
| - | 500.0 °C | Elastic modulus of 158 - 165 GPa |
| - | 540.0 °C | Elastic modulus of 155.13 GPa |
| - | 595.0 °C | Elastic modulus of 151 GPa |
| - | 600.0 °C | Elastic modulus of 150 GPa |
| - | 650.0 °C | Elastic modulus of 146.17 GPa |
| - | 700.0 °C | Elastic modulus of 142 GPa |
| - | 705.0 °C | Elastic modulus of 140.65 GPa |
| - | 760.0 °C | Elastic modulus of 135.83 GPa |
| - | 800.0 °C | Elastic modulus of 134 GPa |
| - | 815.0 °C | Elastic modulus of 131.69 GPa |
| - | 900.0 °C | Elastic modulus of 127 GPa |
| - | 1000.0 °C | Elastic modulus of 120 GPa |
| Elongation | 20.0 °C | Elongation of 35 % |
| Elongation, transverse | 20.0 °C | Elongation, transverse of 30 % |
| Poisson's ratio | 20.0 °C | Poisson's ratio of 0.29 [-] |
| - | 95.0 °C | Poisson's ratio of 0.3 [-] |
| - | 150.0 °C | Poisson's ratio of 0.29 [-] |
| - | 205.0 °C | Poisson's ratio of 0.29 [-] |
| - | 260.0 °C | Poisson's ratio of 0.3 [-] |
| - | 315.0 °C | Poisson's ratio of 0.3 [-] |
| - | 370.0 °C | Poisson's ratio of 0.3 [-] |
| - | 425.0 °C | Poisson's ratio of 0.31 [-] |
| - | 485.0 °C | Poisson's ratio of 0.32 [-] |
| - | 540.0 °C | Poisson's ratio of 0.32 [-] |
| - | 595.0 °C | Poisson's ratio of 0.34 [-] |
| - | 650.0 °C | Poisson's ratio of 0.34 [-] |
| - | 705.0 °C | Poisson's ratio of 0.33 [-] |
| - | 760.0 °C | Poisson's ratio of 0.33 [-] |
| - | 815.0 °C | Poisson's ratio of 0.35 [-] |
| Shear modulus | 20.0 °C | Shear modulus of 77.22 GPa |
| - | 95.0 °C | Shear modulus of 74.46 GPa |
| - | 150.0 °C | Shear modulus of 73.08 GPa |
| - | 205.0 °C | Shear modulus of 71.02 GPa |
| - | 260.0 °C | Shear modulus of 68.26 GPa |
| - | 315.0 °C | Shear modulus of 66.88 GPa |
| - | 370.0 °C | Shear modulus of 64.81 GPa |
| - | 425.0 °C | Shear modulus of 62.74 GPa |
| - | 485.0 °C | Shear modulus of 60.67 GPa |
| - | 540.0 °C | Shear modulus of 58.61 GPa |
| - | 595.0 °C | Shear modulus of 56.54 GPa |
| - | 650.0 °C | Shear modulus of 54.47 GPa |
| - | 705.0 °C | Shear modulus of 53.09 GPa |
| - | 760.0 °C | Shear modulus of 51.02 GPa |
| - | 815.0 °C | Shear modulus of 48.95 GPa |
| Tensile strength | 20.0 °C | Tensile strength of 460 - 730 MPa |
| Tensile strength, transverse | 20.0 °C | Tensile strength, transverse of 460 - 730 MPa |
| Yield strength | 20.0 °C | Yield strength of 180 - 200 MPa |
| Yield strength Rp0.2 | 20.0 °C | Yield strength Rp0.2 of 180 - 200 MPa |
| - | 50.0 °C | Yield strength Rp0.2 of 162 - 190 MPa |
| - | 100.0 °C | Yield strength Rp0.2 of 147 - 176 MPa |
| - | 150.0 °C | Yield strength Rp0.2 of 132 - 167 MPa |
| - | 200.0 °C | Yield strength Rp0.2 of 118 - 157 MPa |
| - | 250.0 °C | Yield strength Rp0.2 of 108 - 147 MPa |
| - | 300.0 °C | Yield strength Rp0.2 of 100 - 136 MPa |
| - | 350.0 °C | Yield strength Rp0.2 of 94 - 130 MPa |
| - | 400.0 °C | Yield strength Rp0.2 of 89 - 125 MPa |
| - | 450.0 °C | Yield strength Rp0.2 of 85 - 121 MPa |
| - | 500.0 °C | Yield strength Rp0.2 of 81 - 119 MPa |
| - | 550.0 °C | Yield strength Rp0.2 of 80 - 118 MPa |
| Yield strength Rp0.2, transverse | 20.0 °C | Yield strength Rp0.2, transverse of 180 - 200 MPa |
| Yield strength Rp1.0 | 20.0 °C | Yield strength Rp1.0 of 215 - 235 MPa |
| - | 50.0 °C | Yield strength Rp1.0 of 201 - 222 MPa |
| - | 100.0 °C | Yield strength Rp1.0 of 181 - 208 MPa |
| - | 150.0 °C | Yield strength Rp1.0 of 162 - 195 MPa |
| - | 200.0 °C | Yield strength Rp1.0 of 147 - 185 MPa |
| - | 250.0 °C | Yield strength Rp1.0 of 137 - 175 MPa |
| - | 300.0 °C | Yield strength Rp1.0 of 127 - 167 MPa |
| - | 350.0 °C | Yield strength Rp1.0 of 121 - 161 MPa |
| - | 400.0 °C | Yield strength Rp1.0 of 116 - 156 MPa |
| - | 450.0 °C | Yield strength Rp1.0 of 112 - 152 MPa |
| - | 500.0 °C | Yield strength Rp1.0 of 109 - 149 MPa |
| - | 550.0 °C | Yield strength Rp1.0 of 108 - 147 MPa |
| Yield strength Rp1.0, transverse | 20.0 °C | Yield strength Rp1.0, transverse of 215 - 235 MPa |
| Yield strength, transverse | 20.0 °C | Yield strength, transverse of 180 - 200 MPa |
Tailor-made steel solutions to meet your unique requirements.
-- Our promise
Similar or equivalent steel materials
- Sandvik 6R35
- DIN 17440 Grade X6CrNiTi18-10 quenched (+Q)
- EN 10028-7 Grade X6CrNiTi18-10 solution annealed (+AT)
- EN 10272 Grade X6CrNiTi18-10 solution annealed (+AT)
- EN 10216-5 Grade X6CrNiTi18-10 solution annealed (+AT)
- DIN 1654-5 Grade X6CrNiTi18-10 quenched (+Q)
- EN 10217-7 Grade X6CrNiTi18-10 solution annealed (+AT)
- EN 10250-4 Grade X6CrNiTi18-10 solution annealed (+AT)
- EN 10222-5 Grade X6CrNiTi18-10 solution annealed (+AT)