EN 10222-5 Grade X2CrNiMo17-12-3 solution annealed (+AT)
EN 10222-5 Grade X2CrNiMo17-12-3 solution annealed (+AT) introduction
The austenitic material X2CrNiMo17-12-3 is used in solution annealed condition in the form of cold rolled band, warm rolled band and warm rolled sheet as well as in the form of rods, wire rods and profiles. It is resistant to intercrystalline corrosion also in sensitized condition.
Equivalent material: GB 022Cr17Ni12Mo2, GB S31603, IS X02Cr17Ni12Mo2, JIS SUSF316L, KS STSF316L, ASTM A965 Grade F316L, UNS S31603, ASTM Grade F316L, ASTM F316L, DIN 1.4432, AFNOR Z3CND17-12-03, BS 316S13, AISI 316L, SAE 316L, JIS SUS316L, JIS SUS316LFB, EN 1.4432, GOST 06Ch17N13M3-WD
EN 10222-5 Grade X2CrNiMo17-12-3 solution annealed (+AT) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 8 g/cm³ |
EN 10222-5 Grade X2CrNiMo17-12-3 solution annealed (+AT) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.6E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.65E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.7E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.75E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.8E-5 1/K |
- |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 500 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 15 W/(m·K) |
- |
EN 10222-5 Grade X2CrNiMo17-12-3 solution annealed (+AT) chemical
| Property |
Value |
| Carbon |
Carbon of 0.03 % |
| Chromium |
Chromium of 16.5 - 18.5 % |
| Manganese |
Manganese of 2 % |
| Molybdenum |
Molybdenum of 2.5 - 3 % |
| Nickel |
Nickel of 10.5 - 13 % |
| Nitrogen |
Nitrogen of 0.1 - 0.11 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.015 % |
EN 10222-5 Grade X2CrNiMo17-12-3 solution annealed (+AT) electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
EN 10222-5 Grade X2CrNiMo17-12-3 solution annealed (+AT) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 200 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 194 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 186 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 179 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 172 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 165 GPa |
- |
| Elongation |
20.0 °C |
Elongation of 35 - 45 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 490 - 690 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 190 MPa |
- |
| Yield strength Rp1.0 |
20.0 °C |
Yield strength Rp1.0 of 225 MPa |
- |
Rely on our strong, dependable steel to support your most critical applications.