EN 10088-1 Grade X2CrNiMo17-12-3 solution annealed (+AT)
EN 10088-1 Grade X2CrNiMo17-12-3 solution annealed (+AT) introduction
The austenitic material X2CrNiMo17-12-3 is used in solution annealed condition in the form of cold rolled strip, warm rolled strip and warm rolled sheet as well as in the form of rods, wire rod and profiles. It is resistant to intercrystalline corrosion also in sensitized condition.
Equivalent material: BS 316S13, GOST 06Ch17N13M3-WD, ISO X2CrNiMo17-12-3, GB 022Cr17Ni12M2, GB S31603, IS X02Cr17Ni12Mo2, IS 316L, ISO 4432-316-03-I, ISO AM32A, JIS SUS316L, GOST 06Х17Н13M3-ВД, KS STS316L, ASTM A240Type316L, ASTM A276Type316L, ASTM A666Type316L, AISI 316L, AISI Type316L, ASTM A959UNSS31603, UNS S31603, DIN 1.4432, AFNOR Z3CND17-12-03, SAE 316L, JIS SUS316LFB, JIS SUSF316L, EN 1.4432
EN 10088-1 Grade X2CrNiMo17-12-3 solution annealed (+AT) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 8 g/cm³ |
EN 10088-1 Grade X2CrNiMo17-12-3 solution annealed (+AT) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.6E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.65E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.7E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.75E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.8E-5 1/K |
- |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 500 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 15 W/(m·K) |
- |
EN 10088-1 Grade X2CrNiMo17-12-3 solution annealed (+AT) chemical
| Property |
Value |
| Carbon |
Carbon of 0.03 % |
| Chromium |
Chromium of 16.5 - 18.5 % |
| Manganese |
Manganese of 2 % |
| Molybdenum |
Molybdenum of 2.5 - 3 % |
| Nickel |
Nickel of 10.5 - 13 % |
| Nitrogen |
Nitrogen of 0.11 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.015 % |
EN 10088-1 Grade X2CrNiMo17-12-3 solution annealed (+AT) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 7.5E-7 Ω·m |
EN 10088-1 Grade X2CrNiMo17-12-3 solution annealed (+AT) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 200 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 194 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 186 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 179 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 172 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 165 GPa |
- |
| Elongation |
20.0 °C |
Elongation of 20 - 40 % |
- |
| Elongation A80, transverse |
20.0 °C |
Elongation A80, transverse of 40 - 45 % |
- |
| Elongation, transverse |
20.0 °C |
Elongation, transverse of 30 - 45 % |
- |
| Hardness, Brinell |
20.0 °C |
Hardness, Brinell of 215 [-] |
- |
| Hardness, Brinell, trans |
20.0 °C |
Hardness, Brinell, trans of 215 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 500 - 1100 MPa |
- |
| Tensile strength, transverse |
20.0 °C |
Tensile strength, transverse of 500 - 700 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 200 - 400 MPa |
- |
| - |
100.0 °C |
Yield strength Rp0.2 of 165 - 166 MPa |
- |
| - |
150.0 °C |
Yield strength Rp0.2 of 150 - 152 MPa |
- |
| - |
200.0 °C |
Yield strength Rp0.2 of 137 MPa |
- |
| - |
250.0 °C |
Yield strength Rp0.2 of 127 MPa |
- |
| - |
300.0 °C |
Yield strength Rp0.2 of 118 - 119 MPa |
- |
| - |
350.0 °C |
Yield strength Rp0.2 of 113 MPa |
- |
| - |
400.0 °C |
Yield strength Rp0.2 of 108 MPa |
- |
| - |
450.0 °C |
Yield strength Rp0.2 of 103 MPa |
- |
| - |
500.0 °C |
Yield strength Rp0.2 of 100 MPa |
- |
| - |
550.0 °C |
Yield strength Rp0.2 of 98 MPa |
- |
| Yield strength Rp0.2, transverse |
20.0 °C |
Yield strength Rp0.2, transverse of 200 - 240 MPa |
- |
| Yield strength Rp1.0 |
20.0 °C |
Yield strength Rp1.0 of 235 MPa |
- |
| - |
100.0 °C |
Yield strength Rp1.0 of 199 - 200 MPa |
- |
| - |
150.0 °C |
Yield strength Rp1.0 of 180 - 181 MPa |
- |
| - |
200.0 °C |
Yield strength Rp1.0 of 165 - 167 MPa |
- |
| - |
250.0 °C |
Yield strength Rp1.0 of 153 - 157 MPa |
- |
| - |
300.0 °C |
Yield strength Rp1.0 of 145 MPa |
- |
| - |
350.0 °C |
Yield strength Rp1.0 of 139 MPa |
- |
| - |
400.0 °C |
Yield strength Rp1.0 of 135 MPa |
- |
| - |
450.0 °C |
Yield strength Rp1.0 of 130 MPa |
- |
| - |
500.0 °C |
Yield strength Rp1.0 of 128 MPa |
- |
| - |
550.0 °C |
Yield strength Rp1.0 of 127 MPa |
- |
| Yield strength Rp1.0, transverse |
20.0 °C |
Yield strength Rp1.0, transverse of 235 - 270 MPa |
- |