EN 10217-3 Grade P460NL2 normalized or normalized formed (+N)
EN 10217-3 Grade P460NL2 normalized or normalized formed (+N) introduction
The steel P460NL2 is a weldable alloy high-grade steel that is especially tough to subzero temperature. Tubes made of this steel are used in the pressure vessel construction, apparatus construction, pipeline construction as well as in the general mechanical engineering and device construction.
Equivalent material: DIN EStE460, DIN 1.8918, DIN EStE 460, EN 1.8918
EN 10217-3 Grade P460NL2 normalized or normalized formed (+N) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.84 g/cm³ |
EN 10217-3 Grade P460NL2 normalized or normalized formed (+N) thermal
| Property |
Temperature |
Value |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.05E-5 1/K |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.15E-5 1/K |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.21E-5 1/K |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.27E-5 1/K |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.32E-5 1/K |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.36E-5 1/K |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.4E-5 1/K |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.44E-5 1/K |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 423 J/(kg·K) |
| - |
20.0 °C |
Specific heat capacity of 461 J/(kg·K) |
| - |
100.0 °C |
Specific heat capacity of 479 J/(kg·K) |
| - |
200.0 °C |
Specific heat capacity of 499 J/(kg·K) |
| - |
300.0 °C |
Specific heat capacity of 517 J/(kg·K) |
| - |
400.0 °C |
Specific heat capacity of 536 J/(kg·K) |
| - |
500.0 °C |
Specific heat capacity of 558 J/(kg·K) |
| - |
600.0 °C |
Specific heat capacity of 587 J/(kg·K) |
| Thermal conductivity |
-100.0 °C |
Thermal conductivity of 34.7 W/(m·K) |
| - |
20.0 °C |
Thermal conductivity of 39.7 W/(m·K) |
| - |
100.0 °C |
Thermal conductivity of 40.9 W/(m·K) |
| - |
200.0 °C |
Thermal conductivity of 41 W/(m·K) |
| - |
300.0 °C |
Thermal conductivity of 39.9 W/(m·K) |
| - |
400.0 °C |
Thermal conductivity of 38.2 W/(m·K) |
| - |
500.0 °C |
Thermal conductivity of 36.1 W/(m·K) |
| - |
600.0 °C |
Thermal conductivity of 33.8 W/(m·K) |
| Thermal diffusivity |
-100.0 °C |
Thermal diffusivity of 11.9 mm²/s |
| - |
20.0 °C |
Thermal diffusivity of 11 mm²/s |
| - |
100.0 °C |
Thermal diffusivity of 10.5 mm²/s |
| - |
200.0 °C |
Thermal diffusivity of 9.9 mm²/s |
| - |
300.0 °C |
Thermal diffusivity of 9.1 mm²/s |
| - |
400.0 °C |
Thermal diffusivity of 8.1 mm²/s |
| - |
500.0 °C |
Thermal diffusivity of 6.9 mm²/s |
| - |
600.0 °C |
Thermal diffusivity of 5.7 mm²/s |
EN 10217-3 Grade P460NL2 normalized or normalized formed (+N) chemical
| Property |
Value |
| Aluminium |
Aluminium of 0.02 % |
| Carbon |
Carbon of 0.2 % |
| Chromium |
Chromium of 0.3 % |
| Copper |
Copper of 0.7 % |
| Manganese |
Manganese of 1 - 1.7 % |
| Molybdenum |
Molybdenum of 0.1 % |
| Nickel |
Nickel of 0.8 % |
| Niobium |
Niobium of 0.05 % |
| Nitrogen |
Nitrogen of 0.02 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.6 % |
| Sulfur |
Sulfur of 0.015 % |
| Titanium |
Titanium of 0.03 % |
| Vanadium |
Vanadium of 0.2 % |
EN 10217-3 Grade P460NL2 normalized or normalized formed (+N) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
-100.0 °C |
Electrical resistivity of 1.97E-7 Ω·m |
| - |
20.0 °C |
Electrical resistivity of 2.62E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 3.13E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 3.85E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 4.7E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 5.69E-7 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 6.85E-7 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 8.2E-7 Ω·m |
EN 10217-3 Grade P460NL2 normalized or normalized formed (+N) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 217 GPa |
- |
| - |
20.0 °C |
Elastic modulus of 212 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 207 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 199 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 192 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 184 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 175 GPa |
- |
| - |
600.0 °C |
Elastic modulus of 164 GPa |
- |
| Elongation |
20.0 °C |
Elongation of 19 % |
- |
| Elongation, transverse |
20.0 °C |
Elongation, transverse of 17 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 560 - 730 MPa |
- |
| Tensile strength, transverse |
20.0 °C |
Tensile strength, transverse of 560 - 730 MPa |
- |
| Yield strength |
20.0 °C |
Yield strength of 440 - 460 MPa |
- |
| Yield strength, transverse |
20.0 °C |
Yield strength, transverse of 440 - 460 MPa |
- |