EN 10028-3 Grade P460NL2 normalized or normalized formed (+N)
EN 10028-3 Grade P460NL2 normalized or normalized formed (+N) introduction
Particularly cryogenic weldable fine grain steel for application in pressure vessel and steel construction.
Equivalent material: GB 15MnVNR, GB L27153, GB 18MnMoNbR, GB A05189, DIN P460NL2, ASTM A612, ASTM A737 Grade C, UNS K12202, DIN 1.8918, IS P460NL2, DIN EStE460, ASTM Grade 70, ASTM C, EN 1.8918, DIN EStE 460
EN 10028-3 Grade P460NL2 normalized or normalized formed (+N) general
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
| Density | 20 °C | Density of 7.84 g/cm³ | normalized or normalized formed (+N) | EN 10028-3 | Sheet, Flat |
EN 10028-3 Grade P460NL2 normalized or normalized formed (+N) thermal
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
| Coefficient of thermal expansion | -100 °C | Coefficient of thermal expansion of 1.05e-05 1/K | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| - | 20 °C | Coefficient of thermal expansion of 1.15e-05 1/K | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| - | 100 °C | Coefficient of thermal expansion of 1.21e-05 1/K | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| - | 200 °C | Coefficient of thermal expansion of 1.27e-05 1/K | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| - | 300 °C | Coefficient of thermal expansion of 1.32e-05 1/K | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| - | 400 °C | Coefficient of thermal expansion of 1.36e-05 1/K | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| - | 500 °C | Coefficient of thermal expansion of 1.4e-05 1/K | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| - | 600 °C | Coefficient of thermal expansion of 1.44e-05 1/K | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| Specific heat capacity | -100 °C | Specific heat capacity of 423 J/(kg·K) | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| - | 20 °C | Specific heat capacity of 430 J/(kg·K) | normalized or normalized formed (+N) | EN 10028-3 | Flat |
| - | 20 °C | Specific heat capacity of 430 - 461 J/(kg·K) | normalized or normalized formed (+N) | EN 10028-3 | Flat |
| - | 20 °C | Specific heat capacity of 461 J/(kg·K) | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| - | 100 °C | Specific heat capacity of 479 J/(kg·K) | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| - | 200 °C | Specific heat capacity of 499 J/(kg·K) | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| - | 300 °C | Specific heat capacity of 517 J/(kg·K) | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| - | 400 °C | Specific heat capacity of 536 J/(kg·K) | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| - | 500 °C | Specific heat capacity of 558 J/(kg·K) | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| - | 600 °C | Specific heat capacity of 587 J/(kg·K) | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| Thermal conductivity | -100 °C | Thermal conductivity of 34.7 W/(m·K) | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| - | 20 °C | Thermal conductivity of 39.7 - 40 W/(m·K) | normalized or normalized formed (+N) | EN 10028-3 | Flat |
| - | 20 °C | Thermal conductivity of 39.7 W/(m·K) | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| - | 20 °C | Thermal conductivity of 40 W/(m·K) | normalized or normalized formed (+N) | EN 10028-3 | Flat |
| - | 100 °C | Thermal conductivity of 40.9 W/(m·K) | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| - | 200 °C | Thermal conductivity of 41 W/(m·K) | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| - | 300 °C | Thermal conductivity of 39.9 W/(m·K) | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| - | 400 °C | Thermal conductivity of 38.2 W/(m·K) | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| - | 500 °C | Thermal conductivity of 36.1 W/(m·K) | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| - | 600 °C | Thermal conductivity of 33.8 W/(m·K) | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| Thermal diffusivity | -100 °C | Thermal diffusivity of 11.9 mm²/s | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| - | 20 °C | Thermal diffusivity of 11 mm²/s | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| - | 100 °C | Thermal diffusivity of 10.5 mm²/s | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| - | 200 °C | Thermal diffusivity of 9.9 mm²/s | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| - | 300 °C | Thermal diffusivity of 9.1 mm²/s | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| - | 400 °C | Thermal diffusivity of 8.1 mm²/s | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| - | 500 °C | Thermal diffusivity of 6.9 mm²/s | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| - | 600 °C | Thermal diffusivity of 5.7 mm²/s | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
EN 10028-3 Grade P460NL2 normalized or normalized formed (+N) chemical
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
| Aluminium | Aluminium of 0.005 % | normalized or normalized formed (+N) | EN 10028-3 | Sheet |
| - | Aluminium of 0.02 % | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| Carbon | Carbon of 0.2 % | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| Chromium | Chromium of 0.3 % | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| Copper | Copper of 0.2 % | normalized or normalized formed (+N) | EN 10028-3 | Sheet |
| - | Copper of 0.7 % | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| Manganese | Manganese of 1 - 1.7 % | normalized or normalized formed (+N) | EN 10028-3 | Sheet |
| - | Manganese of 1.1 - 1.7 % | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| Molybdenum | Molybdenum of 0.1 % | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| Nickel | Nickel of 0.4 % | normalized or normalized formed (+N) | EN 10028-3 | Sheet |
| - | Nickel of 0.8 % | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| Niobium | Niobium of 0.05 % | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| Nitrogen | Nitrogen of 0.025 % | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| Phosphorus | Phosphorus of 0.02 % | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| - | Phosphorus of 0.03 % | normalized or normalized formed (+N) | EN 10028-3 | Sheet |
| Silicon | Silicon of 0.1 - 0.6 % | normalized or normalized formed (+N) | EN 10028-3 | Sheet |
| - | Silicon of 0.6 % | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| Sulfur | Sulfur of 0.01 % | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| - | Sulfur of 0.02 % | normalized or normalized formed (+N) | EN 10028-3 | Sheet |
| Titanium | Titanium of 0.03 % | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
| Vanadium | Vanadium of 0.1 - 0.2 % | normalized or normalized formed (+N) | EN 10028-3 | Sheet |
| - | Vanadium of 0.2 % | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet |
EN 10028-3 Grade P460NL2 normalized or normalized formed (+N) electrical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Electrical conductivity | - | Electrical conductivity of 5 S/m | - | - | - | Predicted Value |
| Electrical resistivity | -100 °C | Electrical resistivity of 1.97e-07 Ω·m | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet | - |
| - | 20 °C | Electrical resistivity of 2.6e-07 Ω·m | normalized or normalized formed (+N) | EN 10028-3 | Flat | - |
| - | 20 °C | Electrical resistivity of 2.6e-07 - 2.62e-07 Ω·m | normalized or normalized formed (+N) | EN 10028-3 | Flat | - |
| - | 20 °C | Electrical resistivity of 2.62e-07 Ω·m | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet | - |
| - | 100 °C | Electrical resistivity of 3.13e-07 Ω·m | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet | - |
| - | 200 °C | Electrical resistivity of 3.85e-07 Ω·m | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet | - |
| - | 300 °C | Electrical resistivity of 4.7e-07 Ω·m | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet | - |
| - | 400 °C | Electrical resistivity of 5.69e-07 Ω·m | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet | - |
| - | 500 °C | Electrical resistivity of 6.85e-07 Ω·m | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet | - |
| - | 600 °C | Electrical resistivity of 8.2e-07 Ω·m | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet | - |
EN 10028-3 Grade P460NL2 normalized or normalized formed (+N) mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Elastic modulus | -100 °C | Elastic modulus of 217 GPa | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet | - |
| - | 20 °C | Elastic modulus of 210 GPa | normalized or normalized formed (+N) | EN 10028-3 | Flat | - |
| - | 20 °C | Elastic modulus of 210 - 212 GPa | normalized or normalized formed (+N) | EN 10028-3 | Flat | - |
| - | 20 °C | Elastic modulus of 212 GPa | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet | - |
| - | 100 °C | Elastic modulus of 207 GPa | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet | - |
| - | 200 °C | Elastic modulus of 199 GPa | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet | - |
| - | 300 °C | Elastic modulus of 192 GPa | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet | - |
| - | 400 °C | Elastic modulus of 184 GPa | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet | - |
| - | 500 °C | Elastic modulus of 175 GPa | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet | - |
| - | 600 °C | Elastic modulus of 164 GPa | normalized or normalized formed (+N) | EN 10028-3 | Flat, Sheet | - |
| Elongation | - | Elongation of 13.9 % | - | - | - | Predicted Value, A200 |
| - | - | Elongation of 15.4 % | - | - | - | Predicted Value, A80 |
| - | - | Elongation of 16.4 % | - | - | - | Predicted Value, A80 Transverse |
| - | - | Elongation of 20.0 % | - | - | - | Predicted Value, A50 |
| - | - | Elongation of 20.9 % | - | - | - | Predicted Value, A5 |
| - | 20 °C | Elongation of 16 % | normalized or normalized formed (+N) | EN 10028-3 | Sheet, Flat | - |
| - | 20 °C | Elongation of 17 % | normalized or normalized formed (+N) | EN 10028-3 | Flat | - |
| - | 20 °C | Elongation of 17 % | normalized or normalized formed (+N) | EN 10028-3 | Sheet | Transverse |
| Hardness, Brinell | - | Hardness, Brinell of 252 [-] | - | - | - | Predicted Value, Transverse |
| Poisson's ratio | - | Poisson's ratio of 0.3 [-] | - | - | - | Typical for Steel |
| Reduction of area | - | Reduction of area of 38.7 % | - | - | - | Predicted Value |
| - | - | Reduction of area of 44.0 % | - | - | - | Predicted Value, Transverse |
| Shear modulus | - | Shear modulus of 80.3 GPa | - | - | - | Predicted Value |
| Shear strength | - | Shear strength of 547.9 MPa | - | - | - | Predicted Value |
| Tensile strength | 20 °C | Tensile strength of 510 - 690 MPa | normalized or normalized formed (+N) | EN 10028-3 | Sheet, Flat | - |
| - | 20 °C | Tensile strength of 510 - 720 MPa | normalized or normalized formed (+N) | EN 10028-3 | Flat | - |
| - | 20 °C | Tensile strength of 510 - 710 MPa | normalized or normalized formed (+N) | EN 10028-3 | Flat | - |
| - | 20 °C | Tensile strength of 520 - 720 MPa | normalized or normalized formed (+N) | EN 10028-3 | Flat | - |
| - | 20 °C | Tensile strength of 520 - 710 MPa | normalized or normalized formed (+N) | EN 10028-3 | Flat | - |
| - | 20 °C | Tensile strength of 520 - 690 MPa | normalized or normalized formed (+N) | EN 10028-3 | Flat | - |
| - | 20 °C | Tensile strength of 540 - 720 MPa | normalized or normalized formed (+N) | EN 10028-3 | Flat | - |
| - | 20 °C | Tensile strength of 540 - 710 MPa | normalized or normalized formed (+N) | EN 10028-3 | Flat | - |
| - | 20 °C | Tensile strength of 540 - 690 MPa | normalized or normalized formed (+N) | EN 10028-3 | Flat | - |
| - | 20 °C | Tensile strength of 570 - 720 MPa | normalized or normalized formed (+N) | EN 10028-3 | Flat | - |
| - | 20 °C | Tensile strength of 570 - 710 MPa | normalized or normalized formed (+N) | EN 10028-3 | Flat | - |
| - | 20 °C | Tensile strength of 570 - 690 MPa | normalized or normalized formed (+N) | EN 10028-3 | Flat | - |
| - | 20 °C | Tensile strength of 630 - 725 MPa | normalized or normalized formed (+N) | EN 10028-3 | Sheet | Transverse |
| Yield strength | - | Yield strength of 283.5 MPa | - | - | - | Predicted Value, RP1 |
| - | - | Yield strength of 315.1 MPa | - | - | - | Predicted Value, RP1 Transverse |
| - | - | Yield strength of 432 MPa | - | - | - | Predicted Value, RP02 |
| - | - | Yield strength of 465.3 MPa | - | - | - | Predicted Value, RP02 Transverse |
| - | - | Yield strength of 507.1 MPa | - | - | - | Predicted Value, RP002 |
| - | - | Yield strength of 520.9 MPa | - | - | - | Predicted Value, RP05 |
| - | 20 °C | Yield strength of 370 MPa | normalized or normalized formed (+N) | EN 10028-3 | Sheet, Flat | - |
| - | 20 °C | Yield strength of 380 MPa | normalized or normalized formed (+N) | EN 10028-3 | Flat | - |
| - | 20 °C | Yield strength of 400 MPa | normalized or normalized formed (+N) | EN 10028-3 | Flat | - |
| - | 20 °C | Yield strength of 430 MPa | normalized or normalized formed (+N) | EN 10028-3 | Flat | - |
| - | 20 °C | Yield strength of 445 MPa | normalized or normalized formed (+N) | EN 10028-3 | Flat | - |
| - | 20 °C | Yield strength of 460 MPa | normalized or normalized formed (+N) | EN 10028-3 | Flat | - |
| - | 20 °C | Yield strength of 460 MPa | normalized or normalized formed (+N) | EN 10028-3 | Sheet | Transverse |
Tailor-made steel solutions to meet your unique requirements.
-- Our promise
Similar or equivalent steel materials
- EN 10028-3 Grade P460NL1 normalized or normalized formed (+N)
- EN 10028-3 Grade P460NH normalized or normalized formed (+N)
- EN 10217-3 Grade StE 460 normalized or normalized formed (+N)
- EN 10217-3 Grade P460N normalized or normalized formed (+N)
- EN 10277-2 Grade USt 37-2 turned
- EN 10277-2 Grade RSt 37-2 cold drawn or turned and soft annealed
- EN 10277-2 Grade USt 37-2 cold drawn or turned and soft annealed
- DIN 5512-2 Grade St 37-2 G cold rolled
- EN 10083-1 Grade C25E treated for cold shearing (+S)
- EN 10217-3 Grade EStE 460 normalized or normalized formed (+N)