EN 10213 Grade GP280GH normalized or normalized formed (+N)
EN 10213 Grade GP280GH normalized or normalized formed (+N) introduction
Material GP280GH is applicated at room temperature and increased temperatures.
Equivalent material: DIN 1.0625, DIN GP280GH, AFNOR GP280GH, BS GP280GH, JIS SCPH2, EN 1.0625
EN 10213 Grade GP280GH normalized or normalized formed (+N) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.8 g/cm³ |
EN 10213 Grade GP280GH normalized or normalized formed (+N) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.28E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.36E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.45E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1289 - 1478 °C |
Typical for High Carbon Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 460 J/(kg·K) |
- |
| Thermal conductivity |
50.0 °C |
Thermal conductivity of 45 W/(m·K) |
- |
EN 10213 Grade GP280GH normalized or normalized formed (+N) chemical
| Property |
Value |
| Carbon |
Carbon of 0.18 - 0.25 % |
| Chromium |
Chromium of 0.3 % |
| Copper |
Copper of 0.3 % |
| Manganese |
Manganese of 0.8 - 1.2 % |
| Molybdenum |
Molybdenum of 0.12 % |
| Nickel |
Nickel of 0.4 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.6 % |
| Sulfur |
Sulfur of 0.02 % |
| Vanadium |
Vanadium of 0.03 % |
EN 10213 Grade GP280GH normalized or normalized formed (+N) electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
EN 10213 Grade GP280GH normalized or normalized formed (+N) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for High Carbon Steel |
| Elongation |
20.0 °C |
Elongation of 22 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for High Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 81 GPa |
Typical for High Carbon Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 480 - 640 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 280 MPa |
- |
| - |
100.0 °C |
Yield strength Rp0.2 of 250 MPa |
- |
| - |
200.0 °C |
Yield strength Rp0.2 of 220 MPa |
- |
| - |
300.0 °C |
Yield strength Rp0.2 of 190 MPa |
- |
| - |
350.0 °C |
Yield strength Rp0.2 of 170 MPa |
- |
| - |
400.0 °C |
Yield strength Rp0.2 of 160 MPa |
- |
| - |
450.0 °C |
Yield strength Rp0.2 of 150 MPa |
- |