EN 10210-1 Grade S235JRH cold worked, welded
EN 10210-1 Grade S235JRH cold worked, welded introduction
Hot finished weldable structural hollow sections with circular, square, rectangular or elliptical cross-section for the steel and plant construction, civil engineering and vehicle construction.
Equivalent material: ISO S235JRH, ASTM A501 Grade B, UNS K02401, DIN St37-2, DIN 1.0039, DIN S235JRH, AFNOR S235JRH, BS S235JRH, EN 1.0039, UNS K01500
EN 10210-1 Grade S235JRH cold worked, welded general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
EN 10210-1 Grade S235JRH cold worked, welded thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
EN 10210-1 Grade S235JRH cold worked, welded chemical
| Property |
Value |
| Carbon |
Carbon of 0.17 % |
| Manganese |
Manganese of 1.4 % |
| Nitrogen |
Nitrogen of 9E-3 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Sulfur |
Sulfur of 0.04 % |
EN 10210-1 Grade S235JRH cold worked, welded magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
EN 10210-1 Grade S235JRH cold worked, welded electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
EN 10210-1 Grade S235JRH cold worked, welded mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation |
20.0 °C |
Elongation of 17 - 26 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 350 - 510 MPa |
- |
| Yield strength |
20.0 °C |
Yield strength of 195 - 235 MPa |
- |