EN 10132-4 Grade C60S cold rolled (+CR)
EN 10132-4 Grade C60S cold rolled (+CR) introduction
The steel C60S is used as cold rolled strip for springs and special applications in thicknesses of up to 6 mm and as tempered cold strip in thicknesses from 0.30 to 3.00 mm.
Equivalent material: ASTM A684 Grade 1060, AISI 1060, ASTM G10600, DIN 1.1221, DIN Ck60, DIN C60E, AFNOR XC60, AFNOR C60RR, AFNOR 9160C031, AFNOR 9160/C25, AFNOR XC65, AFNOR C60E, BS 060A62, BS 070M60, BS CS60, BS C60E, BS 60HS, BS 60CS, UNI C60, SS 1678, 1064, SAE 1060, JIS S58C, JIS S60CM, JIS S65CM, JIS S60C-CSP, JIS S65C-CSP, JIS S65C, JIS 30A, JIS 37A, EN C60E, EN 1.1221, ISO C60E, ISO C60E4, ISO CS60, ISO S58C, GOST 60, GOST 60G, GOST 60GA, GB 60, GB U20602, GB/T 60, GB/T CRB970, GB/T U20602, ASTM 1060, UNS G10600, UNS G10640
EN 10132-4 Grade C60S cold rolled (+CR) general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for High Carbon Steel |
EN 10132-4 Grade C60S cold rolled (+CR) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 1/K |
Typical for High Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1289 - 1478 °C |
Typical for High Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 486 J/(kg·K) |
Typical for High Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 36 W/(m·K) |
Typical for High Carbon Steel |
EN 10132-4 Grade C60S cold rolled (+CR) chemical
| Property |
Value |
| Carbon |
Carbon of 0.57 - 0.65 % |
| Chromium |
Chromium of 0.4 % |
| Manganese |
Manganese of 0.6 - 0.9 % |
| Molybdenum |
Molybdenum of 0.1 % |
| Nickel |
Nickel of 0.4 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.15 - 0.35 % |
| Sulfur |
Sulfur of 0.025 % |
EN 10132-4 Grade C60S cold rolled (+CR) electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
EN 10132-4 Grade C60S cold rolled (+CR) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for High Carbon Steel |
| Hardness, Vickers |
20.0 °C |
Hardness, Vickers of 305 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for High Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 81 GPa |
Typical for High Carbon Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 1100 MPa |
- |