EN 10083-1 Grade C30E treated for cold shearing (+S)
EN 10083-1 Grade C30E treated for cold shearing (+S) introduction
Steel C30E is suitable for components of higher dimension and more complex form which have to meet higher requirements to uniformity of qualities and surface appearance in vehicle manufacturing and machine engineering (e.g. gear wheels, steering knuckles, hubs). Lowest working temperature -25 °C.
Equivalent material: GB 30, AFNOR XC32, BS 080M30, ISO C30E4, JIS S30C, ASTM 1030, DIN Ck30, GB U20302, EN 1.1178, IS 30C8, ISO C30E, GOST 30, ASTM A29 Grade 1030, ASTM A510 Grade 1030, ASTM A576 Grade 1030, ASTM A827 Grade 1030, ASTM A830 Grade 1030, UNS G10300, SAE 1030, DIN 1.1178, DIN C30E, AFNOR C30E, BS En5, BS 30CS, BS 30HS, BS 080M30C30E, BS CS30, AISI 1030, JIS S30CM, JIS CS30, ISO CE28E4, ISO CS30, ISO S30C, GB/T 30, GB/T U20302, GB/T ML30
EN 10083-1 Grade C30E treated for cold shearing (+S) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.82 - 7.85 g/cm³ |
EN 10083-1 Grade C30E treated for cold shearing (+S) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.08E-5 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.19E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.11E-5 - 1.25E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.21E-5 - 1.3E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.29E-5 - 1.36E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.35E-5 - 1.41E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.45E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.49E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Max service temperature, long |
- |
Max service temperature, long of -25 - 0 °C |
- |
| Melting point |
- |
Melting point of 1380 - 1514 °C |
Typical for Medium Carbon Steel |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 423 J/(kg·K) |
- |
| - |
20.0 °C |
Specific heat capacity of 460 - 461 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 479 - 480 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 499 - 520 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 517 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 536 - 610 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 558 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 587 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 48 - 50 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 48.9 - 51 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 47.5 - 48.2 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 44.7 - 45.6 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 41.6 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 38.6 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 35.5 W/(m·K) |
- |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 13.3 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 12.6 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 11.5 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 10.2 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 8.9 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 7.5 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 6 mm²/s |
- |
EN 10083-1 Grade C30E treated for cold shearing (+S) chemical
| Property |
Value |
| Carbon |
Carbon of 0.27 - 0.34 % |
| Chromium |
Chromium of 0.4 % |
| Copper |
Copper of 0.3 % |
| Manganese |
Manganese of 0.5 - 0.8 % |
| Molybdenum |
Molybdenum of 0.1 % |
| Nickel |
Nickel of 0.4 % |
| Phosphorus |
Phosphorus of 0.03 - 0.04 % |
| Silicon |
Silicon of 0.1 - 0.4 % |
| Sulfur |
Sulfur of 0.035 % |
EN 10083-1 Grade C30E treated for cold shearing (+S) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 1.2E-7 - 2.17E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 2.62E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 3.32E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 4.2E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 5.23E-7 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 6.41E-7 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 7.8E-7 Ω·m |
EN 10083-1 Grade C30E treated for cold shearing (+S) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 217 GPa |
- |
| - |
20.0 °C |
Elastic modulus of 210 - 212 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 205 - 207 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 195 - 199 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 185 - 192 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 175 - 184 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 175 GPa |
- |
| - |
600.0 °C |
Elastic modulus of 164 GPa |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Medium Carbon Steel |
| Shear modulus |
20.0 °C |
Shear modulus of 81 GPa |
- |