EN 10250-2 Grade C30 normalized and tempered (+NT)
EN 10250-2 Grade C30 normalized and tempered (+NT) introduction
Steel C30 is suitable for parts of higher ductility requirements in vehicle, engine and machine engineering (e.g. bolts, screws, steering knuckles).
Equivalent material: AS S1030, GB 30, GB U20302, IS 3, IS 30C8, JIS S30C, GOST 30, ASTM A521 Grade 1030, SAE 1030, UNS G10300, DIN 1.0528, DIN C30, AFNOR C30, BS C30, BS 30CS, BS 30HS, AISI 1030, JIS S30CM, EN 1.0528, ISO C30, ISO CS30, GB/T 30, GB/T U20302, GB/T ML30
EN 10250-2 Grade C30 normalized and tempered (+NT) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.82 g/cm³ |
EN 10250-2 Grade C30 normalized and tempered (+NT) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.08E-5 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.19E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.25E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.3E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.36E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.41E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.45E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.49E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1380 - 1514 °C |
Typical for Medium Carbon Steel |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 423 J/(kg·K) |
- |
| - |
20.0 °C |
Specific heat capacity of 461 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 479 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 499 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 517 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 536 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 558 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 587 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 48 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 48.9 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 47.5 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 44.7 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 41.6 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 38.6 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 35.5 W/(m·K) |
- |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 13.3 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 12.6 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 11.5 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 10.2 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 8.9 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 7.5 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 6 mm²/s |
- |
EN 10250-2 Grade C30 normalized and tempered (+NT) chemical
| Property |
Value |
| Carbon |
Carbon of 0.27 - 0.34 % |
| Chromium |
Chromium of 0.4 % |
| Manganese |
Manganese of 0.5 - 0.8 % |
| Molybdenum |
Molybdenum of 0.1 % |
| Nickel |
Nickel of 0.4 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Silicon |
Silicon of 0.4 % |
| Sulfur |
Sulfur of 0.045 % |
EN 10250-2 Grade C30 normalized and tempered (+NT) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 2.17E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 2.62E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 3.32E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 4.2E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 5.23E-7 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 6.41E-7 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 7.8E-7 Ω·m |
EN 10250-2 Grade C30 normalized and tempered (+NT) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 217 GPa |
- |
| - |
20.0 °C |
Elastic modulus of 212 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 207 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 199 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 192 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 184 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 175 GPa |
- |
| - |
600.0 °C |
Elastic modulus of 164 GPa |
- |
| Elongation |
20.0 °C |
Elongation of 21 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Medium Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 75 - 80 GPa |
Typical for Carbon Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 460 - 480 MPa |
- |
| Yield strength |
20.0 °C |
Yield strength of 230 - 250 MPa |
- |