EN 10028-4 Grade 11MnNi5-3 normalized and tempered (+NT)
EN 10028-4 Grade 11MnNi5-3 normalized and tempered (+NT) introduction
Cryogenic Ni-alloy steel for pressure vessel construction (mainly liquid gas tanks) and apparatus engineering up to -60 °C.
Equivalent material: GB A01098, GB 09Mn2VDR, DIN 11MnNi5-3, IS 11MnNi5-3, DIN 1.6212, BS 11MnNi5-3, EN 1.6212, ISO 11MnNi5-3, ASTM Grade LF5 Class 1, ASTM Grade LF5 Class 2
EN 10028-4 Grade 11MnNi5-3 normalized and tempered (+NT) general
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
| Density | 20 °C | Density of 7.85 g/cm³ | normalized and tempered (+NT) | EN 10028-4 | Flat |
EN 10028-4 Grade 11MnNi5-3 normalized and tempered (+NT) thermal
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Coefficient of thermal expansion | -100 °C | Coefficient of thermal expansion of 1.05e-05 1/K | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 20 °C | Coefficient of thermal expansion of 1.15e-05 1/K | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 100 °C | Coefficient of thermal expansion of 1.21e-05 1/K | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 200 °C | Coefficient of thermal expansion of 1.27e-05 1/K | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 300 °C | Coefficient of thermal expansion of 1.32e-05 1/K | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 400 °C | Coefficient of thermal expansion of 1.36e-05 1/K | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 500 °C | Coefficient of thermal expansion of 1.4e-05 1/K | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 600 °C | Coefficient of thermal expansion of 1.44e-05 1/K | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| Melting point | - | Melting point of 1316 - 1595 °C | - | - | - | Typical for Nickel Steel |
| Specific heat capacity | -100 °C | Specific heat capacity of 423 J/(kg·K) | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 20 °C | Specific heat capacity of 461 J/(kg·K) | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 100 °C | Specific heat capacity of 479 J/(kg·K) | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 200 °C | Specific heat capacity of 499 J/(kg·K) | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 300 °C | Specific heat capacity of 517 J/(kg·K) | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 400 °C | Specific heat capacity of 536 J/(kg·K) | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 500 °C | Specific heat capacity of 558 J/(kg·K) | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 600 °C | Specific heat capacity of 587 J/(kg·K) | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| Thermal conductivity | 20 °C | Thermal conductivity of 42.5 W/(m·K) | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 100 °C | Thermal conductivity of 43.5 W/(m·K) | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 200 °C | Thermal conductivity of 42.8 W/(m·K) | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 300 °C | Thermal conductivity of 40.9 W/(m·K) | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 400 °C | Thermal conductivity of 39 W/(m·K) | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 500 °C | Thermal conductivity of 36.4 W/(m·K) | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 600 °C | Thermal conductivity of 34.1 W/(m·K) | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| Thermal diffusivity | 20 °C | Thermal diffusivity of 11.7 mm²/s | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 100 °C | Thermal diffusivity of 11.2 mm²/s | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 200 °C | Thermal diffusivity of 10.3 mm²/s | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 300 °C | Thermal diffusivity of 9.3 mm²/s | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 400 °C | Thermal diffusivity of 8.3 mm²/s | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 500 °C | Thermal diffusivity of 7 mm²/s | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 600 °C | Thermal diffusivity of 5.7 mm²/s | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
EN 10028-4 Grade 11MnNi5-3 normalized and tempered (+NT) chemical
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
| Aluminium | Aluminium of 0.02 % | normalized and tempered (+NT) | EN 10028-4 | Flat |
| Carbon | Carbon of 0.14 % | normalized and tempered (+NT) | EN 10028-4 | Flat |
| Manganese | Manganese of 0.7 - 1.5 % | normalized and tempered (+NT) | EN 10028-4 | Flat |
| Nickel | Nickel of 0.3 - 0.8 % | normalized and tempered (+NT) | EN 10028-4 | Flat |
| Niobium | Niobium of 0.05 % | normalized and tempered (+NT) | EN 10028-4 | Flat |
| Phosphorus | Phosphorus of 0.025 % | normalized and tempered (+NT) | EN 10028-4 | Flat |
| Silicon | Silicon of 0.5 % | normalized and tempered (+NT) | EN 10028-4 | Flat |
| Sulfur | Sulfur of 0.01 % | normalized and tempered (+NT) | EN 10028-4 | Flat |
| - | Sulfur of 0.015 % | normalized and tempered (+NT) | EN 10028-4 | Flat |
| Vanadium | Vanadium of 0.05 % | normalized and tempered (+NT) | EN 10028-4 | Flat |
EN 10028-4 Grade 11MnNi5-3 normalized and tempered (+NT) electrical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Electrical conductivity | - | Electrical conductivity of 6 S/m | - | - | - | Predicted Value |
| Electrical resistivity | 20 °C | Electrical resistivity of 2.45e-07 Ω·m | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 100 °C | Electrical resistivity of 2.94e-07 Ω·m | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 200 °C | Electrical resistivity of 3.69e-07 Ω·m | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 300 °C | Electrical resistivity of 4.59e-07 Ω·m | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 400 °C | Electrical resistivity of 5.58e-07 Ω·m | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 500 °C | Electrical resistivity of 6.79e-07 Ω·m | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 600 °C | Electrical resistivity of 8.13e-07 Ω·m | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
EN 10028-4 Grade 11MnNi5-3 normalized and tempered (+NT) mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Elastic modulus | -100 °C | Elastic modulus of 217 GPa | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 20 °C | Elastic modulus of 212 GPa | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 100 °C | Elastic modulus of 207 GPa | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 200 °C | Elastic modulus of 199 GPa | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 300 °C | Elastic modulus of 192 GPa | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 400 °C | Elastic modulus of 184 GPa | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 500 °C | Elastic modulus of 175 GPa | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 600 °C | Elastic modulus of 164 GPa | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| Elongation | - | Elongation of 18.6 % | - | - | - | Predicted Value, A200 |
| - | - | Elongation of 18.9 % | - | - | - | Predicted Value, A80 Transverse |
| - | - | Elongation of 19.6 % | - | - | - | Predicted Value, A80 |
| - | - | Elongation of 21.3 % | - | - | - | Predicted Value, A5 |
| - | - | Elongation of 21.7 % | - | - | - | Predicted Value, A50 |
| - | - | Elongation of 21.8 % | - | - | - | Predicted Value, Transverse |
| - | 20 °C | Elongation of 24 % | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| Poisson's ratio | - | Poisson's ratio of 0.291 [-] | - | - | - | Typical for Nickel Steel |
| Reduction of area | - | Reduction of area of 39.8 % | - | - | - | Predicted Value |
| - | - | Reduction of area of 44.1 % | - | - | - | Predicted Value, Transverse |
| Shear modulus | - | Shear modulus of 76 GPa | - | - | - | Typical for Nickel Steel |
| Shear strength | - | Shear strength of 532.4 MPa | - | - | - | Predicted Value |
| Tensile strength | 20 °C | Tensile strength of 420 - 530 MPa | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| Yield strength | - | Yield strength of 257.4 MPa | - | - | - | Predicted Value, RP1 |
| - | - | Yield strength of 300.2 MPa | - | - | - | Predicted Value, RP1 Transverse |
| - | - | Yield strength of 329 MPa | - | - | - | Predicted Value, RP02 |
| - | - | Yield strength of 342.8 MPa | - | - | - | Predicted Value, Transverse |
| - | - | Yield strength of 380.6 MPa | - | - | - | Predicted Value, RP05 |
| - | - | Yield strength of 463.6 MPa | - | - | - | Predicted Value, RP02 Transverse |
| - | - | Yield strength of 463.8 MPa | - | - | - | Predicted Value, RP002 |
| - | 20 °C | Yield strength of 265 MPa | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 20 °C | Yield strength of 275 MPa | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
| - | 20 °C | Yield strength of 285 MPa | normalized and tempered (+NT) | EN 10028-4 | Flat | - |
Our steel is the foundation for safe and reliable infrastructure projects.
-- Our promise
Similar or equivalent steel materials
- EN 10028-4 Grade 13MnNi6-3 normalized and tempered (+NT)
- EN 10222-3 Grade 13MnNi6-3 normalized and tempered (+NT)
- DIN 17173 Grade 11MnNi5-3 normalized or normalized formed (+N)
- DIN 17173 Grade 13MnNi6-3 normalized or normalized formed (+N)
- DIN 17174 Grade 11MnNi5-3 normalized or normalized formed (+N)
- DIN 17174 Grade 13MnNi6-3 normalized or normalized formed (+N)
- DIN 17280 Grade 11MnNi5-3 normalized or normalized formed (+N)
- DIN 17280 Grade 13MnNi6-3 normalized or normalized formed (+N)
- ASTM A350 Grade LF5 Class 1 Heat-Treated
- JIS G5152 Grade SCPL21