ASTM A350 Grade LF5 Class 1 Heat-Treated
Equivalent material: DIN 1.5622, DIN 14Ni6, AFNOR 16N6, UNI 14Ni6, UNE 15Ni6, JIS SL2N255, JIS SL2N26, EN 1.5622, ISO 14Ni9, ASTM Grade LF5 Class 2, DIN 1.5633, DIN GS-24Ni8, DIN 24Ni8, AFNOR 20N8, JIS SCPL21, EN 1.5633, DIN 1.6212, DIN 11MnNi5-3, BS 11MnNi5-3, EN 11MnNi5-3, EN 1.6212, ISO 11MnNi5-3, DIN 1.6217, DIN 13MnNi6-3, BS 13MnNi6-3, EN 13MnNi6-3, EN 1.6217, ISO 13MnNi6-3
ASTM A350 Grade LF5 Class 1 Heat-Treated general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 8.8 g/cm³ |
Typical for Nickel Steel |
ASTM A350 Grade LF5 Class 1 Heat-Treated thermal
| Property |
Temperature |
Value |
Comment |
| Melting point |
- |
Melting point of 1316 - 1595 °C |
Typical for Nickel Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 456 J/(kg·K) |
Typical for Nickel Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 10 - 50 W/(m·K) |
Typical for Nickel Steel |
ASTM A350 Grade LF5 Class 1 Heat-Treated chemical
| Property |
Value |
| Carbon |
Carbon of 0.3 % |
| Chromium |
Chromium of 0.3 % |
| Copper |
Copper of 0.4 % |
| Manganese |
Manganese of 0.6 - 1.35 % |
| Molybdenum |
Molybdenum of 0.12 % |
| Nickel |
Nickel of 1 - 2 % |
| Niobium |
Niobium of 0.02 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 0.2 - 0.35 % |
| Sulfur |
Sulfur of 0.04 % |
| Vanadium |
Vanadium of 0.03 % |
ASTM A350 Grade LF5 Class 1 Heat-Treated mechanical
| Property |
Temperature |
Value |
Comment |
| Charpy impact energy |
23.0 °C |
Charpy impact energy of 20 J |
- |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Nickel Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 28 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Nickel Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 38 % |
- |
| Shear modulus |
23.0 °C |
Shear modulus of 76 GPa |
Typical for Nickel Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 415 - 585 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 205 MPa |
- |