DIN 17173 Grade 13MnNi6-3 normalized or normalized formed (+N)
Equivalent material: EN 13MnNi6-3, DIN 1.6217, BS 13MnNi6-3, EN 1.6217, ISO 13MnNi6-3, ASTM Grade LF5 Class 1, ASTM Grade LF5 Class 2
DIN 17173 Grade 13MnNi6-3 normalized or normalized formed (+N) general
| Property | Temperature | Value |
|---|---|---|
| Density | 20.0 °C | Density of 7.85 g/cm³ |
DIN 17173 Grade 13MnNi6-3 normalized or normalized formed (+N) thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Coefficient of thermal expansion | -100.0 °C | Coefficient of thermal expansion of 1.05E-5 1/K | - |
| - | 20.0 °C | Coefficient of thermal expansion of 1.15E-5 1/K | - |
| - | 100.0 °C | Coefficient of thermal expansion of 1.21E-5 1/K | - |
| - | 200.0 °C | Coefficient of thermal expansion of 1.27E-5 1/K | - |
| - | 300.0 °C | Coefficient of thermal expansion of 1.32E-5 1/K | - |
| - | 400.0 °C | Coefficient of thermal expansion of 1.36E-5 1/K | - |
| - | 500.0 °C | Coefficient of thermal expansion of 1.4E-5 1/K | - |
| - | 600.0 °C | Coefficient of thermal expansion of 1.44E-5 1/K | - |
| Melting point | - | Melting point of 1316 - 1595 °C | Typical for Nickel Steel |
| Specific heat capacity | -100.0 °C | Specific heat capacity of 423 J/(kg·K) | - |
| - | 20.0 °C | Specific heat capacity of 461 J/(kg·K) | - |
| - | 100.0 °C | Specific heat capacity of 479 J/(kg·K) | - |
| - | 200.0 °C | Specific heat capacity of 499 J/(kg·K) | - |
| - | 300.0 °C | Specific heat capacity of 517 J/(kg·K) | - |
| - | 400.0 °C | Specific heat capacity of 536 J/(kg·K) | - |
| - | 500.0 °C | Specific heat capacity of 558 J/(kg·K) | - |
| - | 600.0 °C | Specific heat capacity of 587 J/(kg·K) | - |
| Thermal conductivity | 20.0 °C | Thermal conductivity of 42.5 W/(m·K) | - |
| - | 100.0 °C | Thermal conductivity of 43.5 W/(m·K) | - |
| - | 200.0 °C | Thermal conductivity of 42.8 W/(m·K) | - |
| - | 300.0 °C | Thermal conductivity of 40.9 W/(m·K) | - |
| - | 400.0 °C | Thermal conductivity of 39 W/(m·K) | - |
| - | 500.0 °C | Thermal conductivity of 36.4 W/(m·K) | - |
| - | 600.0 °C | Thermal conductivity of 34.1 W/(m·K) | - |
| Thermal diffusivity | 20.0 °C | Thermal diffusivity of 11.7 mm²/s | - |
| - | 100.0 °C | Thermal diffusivity of 11.2 mm²/s | - |
| - | 200.0 °C | Thermal diffusivity of 10.3 mm²/s | - |
| - | 300.0 °C | Thermal diffusivity of 9.3 mm²/s | - |
| - | 400.0 °C | Thermal diffusivity of 8.3 mm²/s | - |
| - | 500.0 °C | Thermal diffusivity of 7 mm²/s | - |
| - | 600.0 °C | Thermal diffusivity of 5.7 mm²/s | - |
DIN 17173 Grade 13MnNi6-3 normalized or normalized formed (+N) chemical
| Property | Value |
|---|---|
| Aluminium | Aluminium of 0.02 % |
| Carbon | Carbon of 0.18 % |
| Manganese | Manganese of 0.85 - 1.65 % |
| Nickel | Nickel of 0.3 - 0.85 % |
| Niobium | Niobium of 0.05 % |
| Phosphorus | Phosphorus of 0.03 % |
| Silicon | Silicon of 0.5 % |
| Sulfur | Sulfur of 0.025 % |
| Vanadium | Vanadium of 0.05 % |
DIN 17173 Grade 13MnNi6-3 normalized or normalized formed (+N) electrical
| Property | Temperature | Value |
|---|---|---|
| Electrical resistivity | 20.0 °C | Electrical resistivity of 2.45E-7 Ω·m |
| - | 100.0 °C | Electrical resistivity of 2.94E-7 Ω·m |
| - | 200.0 °C | Electrical resistivity of 3.69E-7 Ω·m |
| - | 300.0 °C | Electrical resistivity of 4.59E-7 Ω·m |
| - | 400.0 °C | Electrical resistivity of 5.58E-7 Ω·m |
| - | 500.0 °C | Electrical resistivity of 6.79E-7 Ω·m |
| - | 600.0 °C | Electrical resistivity of 8.13E-7 Ω·m |
DIN 17173 Grade 13MnNi6-3 normalized or normalized formed (+N) mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | -100.0 °C | Elastic modulus of 217 GPa | - |
| - | 20.0 °C | Elastic modulus of 212 GPa | - |
| - | 100.0 °C | Elastic modulus of 207 GPa | - |
| - | 200.0 °C | Elastic modulus of 199 GPa | - |
| - | 300.0 °C | Elastic modulus of 192 GPa | - |
| - | 400.0 °C | Elastic modulus of 184 GPa | - |
| - | 500.0 °C | Elastic modulus of 175 GPa | - |
| - | 600.0 °C | Elastic modulus of 164 GPa | - |
| Elongation | 20.0 °C | Elongation of 22 % | - |
| Elongation, transverse | 20.0 °C | Elongation, transverse of 20 % | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.29 [-] | Typical for Nickel Steel |
| Shear modulus | 23.0 °C | Shear modulus of 76 GPa | Typical for Nickel Steel |
| Tensile strength | 20.0 °C | Tensile strength of 490 - 610 MPa | - |
| Tensile strength, transverse | 20.0 °C | Tensile strength, transverse of 490 - 610 MPa | - |
| Yield strength | 20.0 °C | Yield strength of 335 - 355 MPa | - |
| Yield strength, transverse | 20.0 °C | Yield strength, transverse of 335 - 355 MPa | - |
Explore the limitless possibilities with our versatile range of steel products, adaptable to a wide array of applications.
-- Our promise
Similar or equivalent steel materials
- EN 10028-4 Grade 11MnNi5-3 normalized and tempered (+NT)
- EN 10028-4 Grade 13MnNi6-3 normalized and tempered (+NT)
- EN 10222-3 Grade 13MnNi6-3 normalized and tempered (+NT)
- DIN 17173 Grade 11MnNi5-3 normalized or normalized formed (+N)
- DIN 17174 Grade 11MnNi5-3 normalized or normalized formed (+N)
- DIN 17174 Grade 13MnNi6-3 normalized or normalized formed (+N)
- DIN 17280 Grade 11MnNi5-3 normalized or normalized formed (+N)
- DIN 17280 Grade 13MnNi6-3 normalized or normalized formed (+N)
- ASTM A350 Grade LF5 Class 1 Heat-Treated
- JIS G5152 Grade SCPL21