EN 10025-3 Grade S355NL material specification properties
EN 10025-3 Grade S355NL introduction
The unalloyed, normalised/normalising rolled quality steel S355NL is a weldable fine-grained steel with a min. yield point of 355 N/mm². The steel is applicated in normalized condition for several types of welded constructions such as fixed and movable storage container, high-pressure pipes, bridge and load-bearing constructions etc.Cold forming: Suitability for cold bending, folding, cold flanging or cold welting has to be agreed. For sheet, strip and wide flat steel in normalized condition, for nominal thickness (s) up to 16 mm can be warranted the following bending radius values:
longitudinal: 2,5 x s
transverse: 2,0 x s
Sheet and strip of nominal thicknesses
Equivalent material: GB Q345q-D, GB L13454, IS S355NE, ASTM A633 Grade C, ASTM A633 Grade D, UNS K12000, UNS K12037, DIN TStE355, GOST 10G2S1-8, UNI FeE355KTN, DIN 1.0546, EN TStE 355, EN 1.0546, DIN TStE 355, DIN S355NL, AFNOR S355NL, AFNOR E355FP, UNI FeE355 KTN, UNE AE355 KT, BS S355NL, BS 50EE, ISO S355NE, GB/T L03453, GB/T L03454, GB/T Q345FT, GB/T L13454, GB/T Q345q-D, UNS K02003
EN 10025-3 Grade S355NL General properties
The General properties requirements of EN 10025-3 Grade S355NL are as follows:
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
| Density | 20 °C | Density of 7.83 g/cm³ | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar |
EN 10025-3 Grade S355NL Thermal properties
The Thermal properties requirements of EN 10025-3 Grade S355NL are as follows:
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Coefficient of thermal expansion | -100 °C | Coefficient of thermal expansion of 1.08e-05 1/K | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 20 °C | Coefficient of thermal expansion of 1.19e-05 1/K | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 100 °C | Coefficient of thermal expansion of 1.25e-05 1/K | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 200 °C | Coefficient of thermal expansion of 1.3e-05 1/K | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 300 °C | Coefficient of thermal expansion of 1.36e-05 1/K | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 400 °C | Coefficient of thermal expansion of 1.41e-05 1/K | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 500 °C | Coefficient of thermal expansion of 1.45e-05 1/K | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 600 °C | Coefficient of thermal expansion of 1.49e-05 1/K | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| Max service temperature | - | Max service temperature of 368.7 °C | - | - | - | Predicted Value, Long |
| - | - | Max service temperature of 500 °C | - | - | - | Typical for Carbon Steel |
| Melting point | - | Melting point of 1480 - 1526 °C | - | - | - | Typical for Low Carbon Steel |
| Specific heat capacity | -100 °C | Specific heat capacity of 423 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 20 °C | Specific heat capacity of 461 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 100 °C | Specific heat capacity of 479 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 200 °C | Specific heat capacity of 499 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 300 °C | Specific heat capacity of 517 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 400 °C | Specific heat capacity of 536 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 500 °C | Specific heat capacity of 558 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 600 °C | Specific heat capacity of 587 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| Thermal conductivity | -100 °C | Thermal conductivity of 37.6 W/(m·K) | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 20 °C | Thermal conductivity of 42.2 W/(m·K) | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 100 °C | Thermal conductivity of 43.2 W/(m·K) | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 200 °C | Thermal conductivity of 42.9 W/(m·K) | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 300 °C | Thermal conductivity of 41.2 W/(m·K) | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 400 °C | Thermal conductivity of 39.1 W/(m·K) | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 500 °C | Thermal conductivity of 36.6 W/(m·K) | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 600 °C | Thermal conductivity of 34.1 W/(m·K) | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| Thermal diffusivity | -100 °C | Thermal diffusivity of 12.9 mm²/s | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 20 °C | Thermal diffusivity of 11.7 mm²/s | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 100 °C | Thermal diffusivity of 11.2 mm²/s | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 200 °C | Thermal diffusivity of 10.3 mm²/s | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 300 °C | Thermal diffusivity of 9.4 mm²/s | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 400 °C | Thermal diffusivity of 8.3 mm²/s | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 500 °C | Thermal diffusivity of 7.1 mm²/s | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 600 °C | Thermal diffusivity of 5.7 mm²/s | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
EN 10025-3 Grade S355NL Chemical composition
The Chemical composition requirements of EN 10025-3 Grade S355NL are as follows:
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
| Aluminium | Aluminium of 0.02 % | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar |
| Carbon | Carbon of 0.18 % | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar |
| Chromium | Chromium of 0.3 % | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar |
| Copper | Copper of 0.35 % | normalized or normalized formed (+N) | EN 10113-2, EN 10025-3 | Sheet, Strip, Bar, Flat |
| - | Copper of 0.55 % | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire |
| Manganese | Manganese of 0.9 - 1.65 % | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar |
| Molybdenum | Molybdenum of 0.1 % | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar |
| Nickel | Nickel of 0.5 % | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar |
| Niobium | Niobium of 0.05 % | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar |
| Nitrogen | Nitrogen of 0.015 % | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar |
| Phosphorus | Phosphorus of 0.025 % | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire |
| - | Phosphorus of 0.03 % | normalized or normalized formed (+N) | EN 10113-2, EN 10025-3 | Sheet, Strip, Bar, Flat |
| Silicon | Silicon of 0.5 % | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar |
| Sulfur | Sulfur of 0.02 % | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire |
| - | Sulfur of 0.025 % | normalized or normalized formed (+N) | EN 10113-2, EN 10025-3 | Sheet, Strip, Bar, Flat |
| Titanium | Titanium of 0.03 % | normalized or normalized formed (+N) | EN 10113-2, EN 10025-3 | Sheet, Strip, Bar, Flat |
| - | Titanium of 0.05 % | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire |
| Vanadium | Vanadium of 0.12 % | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar |
EN 10025-3 Grade S355NL Magnetic properties
The Magnetic properties requirements of EN 10025-3 Grade S355NL are as follows:
| Property | Value | Comment |
|---|---|---|
| Curie temperature | Curie temperature of 770 °C | Typical for Low Carbon Steel |
EN 10025-3 Grade S355NL Electrical parameters
The Electrical parameters requirements of EN 10025-3 Grade S355NL are as follows:
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Electrical conductivity | - | Electrical conductivity of 5 S/m | - | - | - | Predicted Value |
| Electrical resistivity | -100 °C | Electrical resistivity of 1.82e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 20 °C | Electrical resistivity of 2.47e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 100 °C | Electrical resistivity of 2.96e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 200 °C | Electrical resistivity of 3.68e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 300 °C | Electrical resistivity of 4.55e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 400 °C | Electrical resistivity of 5.56e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 500 °C | Electrical resistivity of 6.75e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 600 °C | Electrical resistivity of 8.13e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
EN 10025-3 Grade S355NL Mechanical properties
The Mechanical properties requirements of EN 10025-3 Grade S355NL are as follows:
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Elastic modulus | -100 °C | Elastic modulus of 217 GPa | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 20 °C | Elastic modulus of 212 GPa | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 100 °C | Elastic modulus of 207 GPa | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 200 °C | Elastic modulus of 199 GPa | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 300 °C | Elastic modulus of 192 GPa | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 400 °C | Elastic modulus of 184 GPa | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 500 °C | Elastic modulus of 175 GPa | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| - | 600 °C | Elastic modulus of 164 GPa | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire, Bar | - |
| Elongation | - | Elongation of 17.0 % | - | - | - | Predicted Value, A80 Transverse |
| - | - | Elongation of 17.3 % | - | - | - | Predicted Value, A80 |
| - | - | Elongation of 17.9 % | - | - | - | Predicted Value, A200 |
| - | - | Elongation of 19.6 % | - | - | - | Predicted Value, Transverse |
| - | - | Elongation of 21.1 % | - | - | - | Predicted Value, A5 |
| - | - | Elongation of 21.4 % | - | - | - | Predicted Value, A50 |
| - | 20 °C | Elongation of 20 % | normalized or normalized formed (+N) | EN 10113-2, EN 10025-3 | Sheet, Flat | - |
| - | 20 °C | Elongation of 21 % | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Elongation of 22 % | normalized or normalized formed (+N) | EN 10113-2, EN 10025-3 | Sheet, Strip, Bar, Flat, Rod, Wire | - |
| Hardness, Brinell | - | Hardness, Brinell of 243 [-] | - | - | - | Predicted Value, Transverse |
| Poisson's ratio | - | Poisson's ratio of 0.29 [-] | - | - | - | Typical for Low Carbon Steel |
| Reduction of area | - | Reduction of area of 43.8 % | - | - | - | Predicted Value, Transverse |
| - | - | Reduction of area of 52.2 % | - | - | - | Predicted Value |
| Shear modulus | - | Shear modulus of 82 GPa | - | - | - | Typical for Low Carbon Steel |
| Shear strength | - | Shear strength of 513.5 MPa | - | - | - | Predicted Value |
| Tensile strength | 20 °C | Tensile strength of 440 - 590 MPa | normalized or normalized formed (+N) | EN 10113-2, EN 10025-3 | Sheet, Flat | - |
| - | 20 °C | Tensile strength of 450 - 630 MPa | normalized or normalized formed (+N) | EN 10113-2, EN 10025-3 | Sheet, Strip, Bar, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 450 - 600 MPa | normalized or normalized formed (+N) | EN 10113-2, EN 10025-3 | Sheet, Strip, Bar, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 470 - 630 MPa | normalized or normalized formed (+N) | EN 10113-2, EN 10025-3 | Sheet, Strip, Bar, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 470 - 600 MPa | normalized or normalized formed (+N) | EN 10113-2, EN 10025-3 | Sheet, Strip, Bar, Flat, Rod, Wire | - |
| Yield strength | - | Yield strength of 254.1 MPa | - | - | - | Predicted Value, RP1 |
| - | - | Yield strength of 301.2 MPa | - | - | - | Predicted Value, RP1 Transverse |
| - | - | Yield strength of 360.3 MPa | - | - | - | Predicted Value, RP02 |
| - | - | Yield strength of 376.2 MPa | - | - | - | Predicted Value, Transverse |
| - | - | Yield strength of 453.9 MPa | - | - | - | Predicted Value, RP02 Transverse |
| - | - | Yield strength of 462.2 MPa | - | - | - | Predicted Value, RP002 |
| - | - | Yield strength of 465.6 MPa | - | - | - | Predicted Value, RP05 |
| - | 20 °C | Yield strength of 275 MPa | normalized or normalized formed (+N) | EN 10025-3, EN 10113-2 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Yield strength of 285 MPa | normalized or normalized formed (+N) | EN 10113-2, EN 10025-3 | Sheet, Flat, Strip, Rod, Wire | - |
| - | 20 °C | Yield strength of 295 MPa | normalized or normalized formed (+N) | EN 10113-2, EN 10025-3 | Sheet, Strip, Bar, Flat, Rod, Wire | - |
| - | 20 °C | Yield strength of 315 MPa | normalized or normalized formed (+N) | EN 10113-2, EN 10025-3 | Sheet, Strip, Bar, Flat, Rod, Wire | - |
| - | 20 °C | Yield strength of 325 MPa | normalized or normalized formed (+N) | EN 10113-2, EN 10025-3 | Sheet, Strip, Bar, Flat, Rod, Wire | - |
| - | 20 °C | Yield strength of 335 MPa | normalized or normalized formed (+N) | EN 10113-2, EN 10025-3 | Sheet, Strip, Bar, Flat, Rod, Wire | - |
| - | 20 °C | Yield strength of 345 MPa | normalized or normalized formed (+N) | EN 10113-2, EN 10025-3 | Sheet, Strip, Bar, Flat, Rod, Wire | - |
| - | 20 °C | Yield strength of 355 MPa | normalized or normalized formed (+N) | EN 10113-2, EN 10025-3 | Sheet, Strip, Bar, Flat, Rod, Wire | - |
Experience the power of our premium steel, forged to perfection for exceptional performance.
-- Our promise
Similar or equivalent steel materials
- EN 10028-3 Grade P355NL1 normalized or normalized formed (+N)
- EN 10025-3 Grade S355N normalized or normalized formed (+N)
- EN 10028-3 Grade P355N normalized or normalized formed (+N)
- EN 10217-3 Grade TStE 355 normalized or normalized formed (+N)
- DIN 17125 Grade TStE 355 normalized or normalized formed (+N)
- EN 10216-3 Grade P355NL1 normalized or normalized formed (+N)
- EN 10217-3 Grade P355NL1 normalized or normalized formed (+N)
- DIN 17103 Grade TStE 355 cold worked, welded and normalized
- DIN 2393-2 Grade St 52-3 bright drawn soft
- DIN 2393-2 Grade St 52-3 bright drawn hard
Get a quote