DIN 17445 Grade G-X6CrNiMo18-10 quenched (+Q)
DIN 17445 Grade G-X6CrNiMo18-10 quenched (+Q) introduction
G-X 6 CrNiMo 18 10, for armatures, pumps, mixers, filters, vessels for the chemical industry, textile industry, rayon industry, cellulose industry
Equivalent material: ISO C60, ISO C60H, DIN 1.4408, DIN GX5CrNiMo19-11-2, JIS SCS14A, EN GX5CrNiMo19-11-2, EN 1.4408
DIN 17445 Grade G-X6CrNiMo18-10 quenched (+Q) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.9 g/cm³ |
DIN 17445 Grade G-X6CrNiMo18-10 quenched (+Q) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.65E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.75E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.75E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.85E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.85E-5 1/K |
- |
| Max service temperature, long |
- |
Max service temperature, long of -196 - 550 °C |
- |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 500 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 15 W/(m·K) |
- |
DIN 17445 Grade G-X6CrNiMo18-10 quenched (+Q) chemical
| Property |
Value |
| Carbon |
Carbon of 0.07 % |
| Chromium |
Chromium of 18 - 20 % |
| Manganese |
Manganese of 1.5 % |
| Molybdenum |
Molybdenum of 2 - 3 % |
| Nickel |
Nickel of 10 - 12 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Silicon |
Silicon of 1.5 % |
| Sulfur |
Sulfur of 0.03 % |
DIN 17445 Grade G-X6CrNiMo18-10 quenched (+Q) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 7.5E-7 Ω·m |
DIN 17445 Grade G-X6CrNiMo18-10 quenched (+Q) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Elongation |
20.0 °C |
Elongation of 20 % |
- |
| Hardness, Brinell |
20.0 °C |
Hardness, Brinell of 130 - 200 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 440 - 640 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 185 MPa |
- |
| - |
100.0 °C |
Yield strength Rp0.2 of 150 MPa |
- |
| - |
150.0 °C |
Yield strength Rp0.2 of 130 MPa |
- |
| - |
200.0 °C |
Yield strength Rp0.2 of 120 MPa |
- |
| - |
250.0 °C |
Yield strength Rp0.2 of 110 MPa |
- |
| - |
300.0 °C |
Yield strength Rp0.2 of 100 MPa |
- |
| Yield strength Rp1.0 |
20.0 °C |
Yield strength Rp1.0 of 210 MPa |
- |
| - |
100.0 °C |
Yield strength Rp1.0 of 175 MPa |
- |
| - |
150.0 °C |
Yield strength Rp1.0 of 155 MPa |
- |
| - |
200.0 °C |
Yield strength Rp1.0 of 145 MPa |
- |
| - |
250.0 °C |
Yield strength Rp1.0 of 135 MPa |
- |
| - |
300.0 °C |
Yield strength Rp1.0 of 125 MPa |
- |