DIN 17120 Grade USt37-2

DIN 17120 Grade USt37-2

Equivalent material: DIN 1.0036, DIN S235JRG1, UNI FE37BFU, EN S235JRG1, EN 1.0036, GOST St3kp, GOST 18kp, GOST 16D, GB/T Q235, GB/T U12352, GB/T Q235B, UNS K02502

DIN 17120 Grade USt37-2 general

Property Temperature Value
Density 20.0 °C Density of 7.85 g/cm³

DIN 17120 Grade USt37-2 thermal

Property Temperature Value Comment
Coefficient of thermal expansion -100.0 °C Coefficient of thermal expansion of 1.08E-5 1/K -
- 20.0 °C Coefficient of thermal expansion of 1.19E-5 1/K -
- 100.0 °C Coefficient of thermal expansion of 1.25E-5 1/K -
- 200.0 °C Coefficient of thermal expansion of 1.3E-5 1/K -
- 300.0 °C Coefficient of thermal expansion of 1.36E-5 1/K -
- 400.0 °C Coefficient of thermal expansion of 1.41E-5 1/K -
- 500.0 °C Coefficient of thermal expansion of 1.45E-5 1/K -
- 600.0 °C Coefficient of thermal expansion of 1.49E-5 1/K -
Max service temperature - Max service temperature of 500 °C Typical for Carbon Steel
Melting point - Melting point of 1480 - 1526 °C Typical for Low Carbon Steel
Specific heat capacity -100.0 °C Specific heat capacity of 423 J/(kg·K) -
- 20.0 °C Specific heat capacity of 461 J/(kg·K) -
- 100.0 °C Specific heat capacity of 479 J/(kg·K) -
- 200.0 °C Specific heat capacity of 499 J/(kg·K) -
- 300.0 °C Specific heat capacity of 517 J/(kg·K) -
- 400.0 °C Specific heat capacity of 536 J/(kg·K) -
- 500.0 °C Specific heat capacity of 558 J/(kg·K) -
- 600.0 °C Specific heat capacity of 587 J/(kg·K) -
Thermal conductivity 20.0 °C Thermal conductivity of 56.9 W/(m·K) -
- 100.0 °C Thermal conductivity of 56.4 W/(m·K) -
- 200.0 °C Thermal conductivity of 53.5 W/(m·K) -
- 300.0 °C Thermal conductivity of 49.4 W/(m·K) -
- 400.0 °C Thermal conductivity of 45.2 W/(m·K) -
- 500.0 °C Thermal conductivity of 41.3 W/(m·K) -
- 600.0 °C Thermal conductivity of 37.6 W/(m·K) -
Thermal diffusivity 20.0 °C Thermal diffusivity of 15.7 mm²/s -
- 100.0 °C Thermal diffusivity of 14.5 mm²/s -
- 200.0 °C Thermal diffusivity of 12.9 mm²/s -
- 300.0 °C Thermal diffusivity of 11.2 mm²/s -
- 400.0 °C Thermal diffusivity of 9.6 mm²/s -
- 500.0 °C Thermal diffusivity of 7.9 mm²/s -
- 600.0 °C Thermal diffusivity of 6.3 mm²/s -

DIN 17120 Grade USt37-2 chemical

Property Value
Carbon Carbon of 0.17 %
Nitrogen Nitrogen of 7E-3 %
Phosphorus Phosphorus of 0.05 %
Sulfur Sulfur of 0.05 %

DIN 17120 Grade USt37-2 magnetic

Property Value Comment
Curie temperature Curie temperature of 770 °C Typical for Low Carbon Steel

DIN 17120 Grade USt37-2 electrical

Property Temperature Value
Electrical resistivity 20.0 °C Electrical resistivity of 1.83E-7 Ω·m
- 100.0 °C Electrical resistivity of 2.27E-7 Ω·m
- 200.0 °C Electrical resistivity of 2.95E-7 Ω·m
- 300.0 °C Electrical resistivity of 3.8E-7 Ω·m
- 400.0 °C Electrical resistivity of 4.81E-7 Ω·m
- 500.0 °C Electrical resistivity of 5.99E-7 Ω·m
- 600.0 °C Electrical resistivity of 7.38E-7 Ω·m

DIN 17120 Grade USt37-2 mechanical

Property Temperature Value Comment
Elastic modulus -100.0 °C Elastic modulus of 217 GPa -
- 20.0 °C Elastic modulus of 212 GPa -
- 100.0 °C Elastic modulus of 207 GPa -
- 200.0 °C Elastic modulus of 199 GPa -
- 300.0 °C Elastic modulus of 192 GPa -
- 400.0 °C Elastic modulus of 184 GPa -
- 500.0 °C Elastic modulus of 175 GPa -
- 600.0 °C Elastic modulus of 164 GPa -
Elongation 20.0 °C Elongation of 26 % -
Elongation, transverse 20.0 °C Elongation, transverse of 24 % -
Poisson's ratio 23.0 °C Poisson's ratio of 0.29 [-] Typical for Low Carbon Steel
Shear modulus 23.0 °C Shear modulus of 82 GPa Typical for Low Carbon Steel
Tensile strength 20.0 °C Tensile strength of 340 - 470 MPa -
Tensile strength, transverse 20.0 °C Tensile strength, transverse of 340 - 470 MPa -
Yield strength 20.0 °C Yield strength of 235 MPa -
Yield strength, transverse 20.0 °C Yield strength, transverse of 235 MPa -