DIN 17103 Grade StE500 normalized or normalized formed (+N)
DIN 17103 Grade StE500 normalized or normalized formed (+N) introduction
The fine grained steel StE 500 is used for welded constructions of different kind like pressure vessels, stationary or mobile storage tanks, high pressure lines, bridge and support constructions etc. The lowest application temperature amounts to -20 °C.
Equivalent material: DIN StE500, DIN 1.8907, DIN S500N, JIS SM570, JIS SM58, EN 1.8907
DIN 17103 Grade StE500 normalized or normalized formed (+N) general
| Property | Temperature | Value |
|---|---|---|
| Density | 20.0 °C | Density of 7.84 g/cm³ |
DIN 17103 Grade StE500 normalized or normalized formed (+N) thermal
| Property | Temperature | Value |
|---|---|---|
| Coefficient of thermal expansion | -100.0 °C | Coefficient of thermal expansion of 1.05E-5 1/K |
| - | 20.0 °C | Coefficient of thermal expansion of 1.15E-5 1/K |
| - | 100.0 °C | Coefficient of thermal expansion of 1.21E-5 1/K |
| - | 200.0 °C | Coefficient of thermal expansion of 1.27E-5 1/K |
| - | 300.0 °C | Coefficient of thermal expansion of 1.32E-5 1/K |
| - | 400.0 °C | Coefficient of thermal expansion of 1.36E-5 1/K |
| - | 500.0 °C | Coefficient of thermal expansion of 1.4E-5 1/K |
| - | 600.0 °C | Coefficient of thermal expansion of 1.44E-5 1/K |
| Max service temperature, long | - | Max service temperature, long of -20 - 0 °C |
| Specific heat capacity | -100.0 °C | Specific heat capacity of 423 J/(kg·K) |
| - | 20.0 °C | Specific heat capacity of 461 J/(kg·K) |
| - | 100.0 °C | Specific heat capacity of 479 J/(kg·K) |
| - | 200.0 °C | Specific heat capacity of 499 J/(kg·K) |
| - | 300.0 °C | Specific heat capacity of 517 J/(kg·K) |
| - | 400.0 °C | Specific heat capacity of 536 J/(kg·K) |
| - | 500.0 °C | Specific heat capacity of 558 J/(kg·K) |
| - | 600.0 °C | Specific heat capacity of 587 J/(kg·K) |
| Thermal conductivity | -100.0 °C | Thermal conductivity of 34.7 W/(m·K) |
| - | 20.0 °C | Thermal conductivity of 39.7 W/(m·K) |
| - | 100.0 °C | Thermal conductivity of 40.9 W/(m·K) |
| - | 200.0 °C | Thermal conductivity of 41 W/(m·K) |
| - | 300.0 °C | Thermal conductivity of 39.9 W/(m·K) |
| - | 400.0 °C | Thermal conductivity of 38.2 W/(m·K) |
| - | 500.0 °C | Thermal conductivity of 36.1 W/(m·K) |
| - | 600.0 °C | Thermal conductivity of 33.8 W/(m·K) |
| Thermal diffusivity | -100.0 °C | Thermal diffusivity of 11.9 mm²/s |
| - | 20.0 °C | Thermal diffusivity of 11 mm²/s |
| - | 100.0 °C | Thermal diffusivity of 10.5 mm²/s |
| - | 200.0 °C | Thermal diffusivity of 9.9 mm²/s |
| - | 300.0 °C | Thermal diffusivity of 9.1 mm²/s |
| - | 400.0 °C | Thermal diffusivity of 8.1 mm²/s |
| - | 500.0 °C | Thermal diffusivity of 6.9 mm²/s |
| - | 600.0 °C | Thermal diffusivity of 5.7 mm²/s |
DIN 17103 Grade StE500 normalized or normalized formed (+N) chemical
| Property | Value |
|---|---|
| Aluminium | Aluminium of 0.02 % |
| Carbon | Carbon of 0.21 % |
| Chromium | Chromium of 0.3 % |
| Copper | Copper of 0.2 % |
| Manganese | Manganese of 1 - 1.7 % |
| Molybdenum | Molybdenum of 0.1 % |
| Nickel | Nickel of 1 % |
| Niobium | Niobium of 0.05 % |
| Nitrogen | Nitrogen of 0.02 % |
| Phosphorus | Phosphorus of 0.04 % |
| Silicon | Silicon of 0.1 - 0.6 % |
| Sulfur | Sulfur of 0.03 % |
| Vanadium | Vanadium of 0.22 % |
DIN 17103 Grade StE500 normalized or normalized formed (+N) electrical
| Property | Temperature | Value |
|---|---|---|
| Electrical resistivity | -100.0 °C | Electrical resistivity of 1.97E-7 Ω·m |
| - | 20.0 °C | Electrical resistivity of 2.62E-7 Ω·m |
| - | 100.0 °C | Electrical resistivity of 3.13E-7 Ω·m |
| - | 200.0 °C | Electrical resistivity of 3.85E-7 Ω·m |
| - | 300.0 °C | Electrical resistivity of 4.7E-7 Ω·m |
| - | 400.0 °C | Electrical resistivity of 5.69E-7 Ω·m |
| - | 500.0 °C | Electrical resistivity of 6.85E-7 Ω·m |
| - | 600.0 °C | Electrical resistivity of 8.2E-7 Ω·m |
DIN 17103 Grade StE500 normalized or normalized formed (+N) mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | -100.0 °C | Elastic modulus of 217 GPa | - |
| - | 20.0 °C | Elastic modulus of 212 GPa | - |
| - | 100.0 °C | Elastic modulus of 207 GPa | - |
| - | 200.0 °C | Elastic modulus of 199 GPa | - |
| - | 300.0 °C | Elastic modulus of 192 GPa | - |
| - | 400.0 °C | Elastic modulus of 184 GPa | - |
| - | 500.0 °C | Elastic modulus of 175 GPa | - |
| - | 600.0 °C | Elastic modulus of 164 GPa | - |
| Elongation | 20.0 °C | Elongation of 16 % | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.3 [-] | Typical for Steel |
| Tensile strength | 20.0 °C | Tensile strength of 570 - 780 MPa | - |
| Yield strength | 20.0 °C | Yield strength of 410 - 500 MPa | - |
Explore the limitless possibilities with our versatile range of steel products, adaptable to a wide array of applications.
-- Our promise
Similar or equivalent steel materials
- EN 10277-2 Grade St60-2 cold drawn
- EN 10277-2 Grade St 60-2 cold drawn or turned and normalized
- EN 10277-2 Grade St 60-2 turned
- EN 10277-2 Grade St 60-2 cold drawn or turned and soft annealed
- EN 10277-2 Grade ZSt60-2 cold drawn or turned and normalized
- EN 10277-2 Grade E335GC cold drawn
- JIS G3445 Grade STKM12C
- EN 10277-2 Grade ZSt60-2 cold drawn or turned and soft annealed
- EN 10277-2 Grade E335GC as rolled and turned (+SH)
- JIS G3136 Grade SN400C
Get a quote