EN 10277-2 Grade E335GC cold drawn
EN 10277-2 Grade E335GC cold drawn introduction
E335GC is applicated as cold drawing grade. The steel is used for wear and strength loaded parts (bolts, shafts, spindles, axles, wedges). It is surface hardenable. As a bright steel product it is used in the form of bars, bright, straight, in various conditions (see DIN EN 10277 : 1999-10).
Equivalent material: DIN ZSt60-2, DIN 1.0543, DIN E335GC, AFNOR E335GC, BS E335GC, JIS SM570, EN 1.0543, ISO Fe 590, GB HRB 335, ASTM Grade 2
EN 10277-2 Grade E335GC cold drawn general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.85 g/cm³ |
EN 10277-2 Grade E335GC cold drawn thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.11E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.21E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.29E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.35E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1380 - 1514 °C |
Typical for Medium Carbon Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 450 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 54 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 50.7 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 46.9 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 41.5 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 39.4 W/(m·K) |
- |
EN 10277-2 Grade E335GC cold drawn magnetic
| Property |
Value |
| Nitrogen |
Nitrogen of 9E-3 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Sulfur |
Sulfur of 0.045 % |
EN 10277-2 Grade E335GC cold drawn electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 2E-7 Ω·m |
EN 10277-2 Grade E335GC cold drawn mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 210 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 205 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 195 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 185 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 175 GPa |
- |
| Elongation |
20.0 °C |
Elongation of 5 - 8 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Medium Carbon Steel |
| Shear modulus |
20.0 °C |
Shear modulus of 81 GPa |
- |
| Tensile strength |
20.0 °C |
Tensile strength of 570 - 1050 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 295 - 540 MPa |
- |
Experience the seamless integration of our steel products into your projects, delivering flawless results every time.