ASTM A815 Grade S43000 Heat-Treated
Equivalent material: DIN 1.4016, DIN X6Cr17, DIN X8Cr17, DIN X3CrTi17, AFNOR Z8C17, BS 430S15, UNI X8Cr17, SS 2320, UNE F.3113, AISI 430, SAE 430, JIS SUS430, JIS SUS430TP, JIS SUS430TB, JIS SUS430TKA, JIS SUS430TKC, JIS SUSY430, EN X6Cr17, EN 1.4016, ISO X6Cr17, ISO F1, GOST 12Ch17, GB 1Cr17, UNS S43000
ASTM A815 Grade S43000 Heat-Treated general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.6 - 7.8 g/cm³ |
Typical for Ferritic Stainless Steel |
ASTM A815 Grade S43000 Heat-Treated thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 9.3E-6 - 1.2E-5 1/K |
Typical for Ferritic Stainless Steel |
| Melting point |
- |
Melting point of 1425 - 1530 °C |
Typical for Ferritic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 420 - 586 J/(kg·K) |
Typical for Ferritic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 11 - 22 W/(m·K) |
Typical for Ferritic Stainless Steel |
ASTM A815 Grade S43000 Heat-Treated chemical
| Property |
Value |
| Carbon |
Carbon of 0.04 % |
| Chromium |
Chromium of 24 - 27 % |
| Copper |
Copper of 1.5 - 2.5 % |
| Manganese |
Manganese of 1.5 % |
| Molybdenum |
Molybdenum of 2.9 - 3.9 % |
| Nickel |
Nickel of 4.5 - 6.5 % |
| Nitrogen |
Nitrogen of 0.1 - 0.25 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.03 % |
ASTM A815 Grade S43000 Heat-Treated electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 6E-7 - 7.5E-7 Ω·m |
Typical for Ferritic Stainless Steel |
ASTM A815 Grade S43000 Heat-Treated mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 220 GPa |
Typical for Ferritic Stainless Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 20 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 190 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Ferritic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Ferritic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 450 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 240 MPa |
- |