ASTM A765 Grade III Normalized and Tempered, Double Normalized and Tempered, or Quenched and Tempered
Equivalent material: DIN 1.0576, DIN RoSt 52-3, DIN St 52-3 N, DIN S355J2H, AFNOR S355J2H, BS S355J2H, BS 50D, AISI 345A, SAE 345A, EN S355J2H, EN 1.0576, ISO S355J2H, ASTM Grade III, UNS K12709, DIN 1.0570, DIN St 52-3, DIN St52-3, DIN S355J2, DIN Fe 510 D1, DIN St 52-3 G, DIN S355J2G3, DIN S325G, AFNOR TU E 355 4, AFNOR TS E 355 4, AFNOR S355J2G3, AFNOR E36-3, BS 50 D, BS S355J2G3, AISI 1024, SAE 1024, JIS SKK490, JIS SM50, JIS SM53, JIS SM490, JIS SM520, JIS STK50, JIS STK51, JIS STK490, JIS STK500, JIS STKR50, JIS STKR490, JIS SM490A, JIS SM490B, JIS SM490C, JIS SM490YA, JIS SM490YB, JIS SM520B, JIS SM520C, JIS SKY490, EN S355J2, EN 1.0570, ISO S355D, GOST 17G1S, GOST 17GS, GB/T 16MnDR, GB/T L20173, GB/T 16Mn, GB/T L20166, ASTM Grade LF2 Class 1, UNS K02003, UNS K03011, UNS K03014, UNS K12037, IS Fe540W-HT
ASTM A765 Grade III Normalized and Tempered, Double Normalized and Tempered, or Quenched and Tempered general
| Property |
Temperature |
Value |
Comment |
| Density |
20.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
ASTM A765 Grade III Normalized and Tempered, Double Normalized and Tempered, or Quenched and Tempered thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
20.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
ASTM A765 Grade III Normalized and Tempered, Double Normalized and Tempered, or Quenched and Tempered chemical
| Property |
Value |
| Aluminium |
Aluminium of 0.05 % |
| Carbon |
Carbon of 0.2 % |
| Chromium |
Chromium of 0.2 % |
| Copper |
Copper of 0.35 % |
| Manganese |
Manganese of 0.9 % |
| Molybdenum |
Molybdenum of 0.06 % |
| Nickel |
Nickel of 3.3 - 3.8 % |
| Phosphorus |
Phosphorus of 0.02 % |
| Silicon |
Silicon of 0.15 - 0.35 % |
| Sulfur |
Sulfur of 0.02 % |
| Vanadium |
Vanadium of 0.05 % |
ASTM A765 Grade III Normalized and Tempered, Double Normalized and Tempered, or Quenched and Tempered magnetic
| Property |
Temperature |
Value |
Comment |
| Curie temperature |
20.0 °C |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
ASTM A765 Grade III Normalized and Tempered, Double Normalized and Tempered, or Quenched and Tempered electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
ASTM A765 Grade III Normalized and Tempered, Double Normalized and Tempered, or Quenched and Tempered mechanical
| Property |
Temperature |
Value |
Comment |
| Charpy impact energy |
20.0 °C |
Charpy impact energy of 20 J |
- |
| Elastic modulus |
20.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation A50 |
20.0 °C |
Elongation A50 of 22 % |
- |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Reduction of area |
20.0 °C |
Reduction of area of 35 % |
- |
| Shear modulus |
20.0 °C |
Shear modulus of 75 - 80 GPa |
Typical for Carbon Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 485 - 655 MPa |
- |
| Yield Strength Rp0.2, short transverse |
20.0 °C |
Yield Strength Rp0.2, short transverse of 260 MPa |
- |