ASTM A752 Grade 5140 Annealed
Equivalent material: DIN 1.7035, DIN 41Cr4, AFNOR 41Cr4, BS 41Cr4, BS 530M40, UNE 41Cr4, AISI 5140, AISI 5140H, SAE 5140, SAE 5140H, JIS SCr440, JIS SCr440WCH, JIS SCr440H, JIS SCr440M, EN 41Cr4, EN 1.7035, GOST 41H, GOST 40Ch, GOST 38ChA, GB 40Cr, GB/T 40Cr, GB/T A20402, UNS H51400, UNS G51400, IS 40Cr1, IS 40Cr4
ASTM A752 Grade 5140 Annealed general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Chromium Steel |
ASTM A752 Grade 5140 Annealed thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 9.4E-6 - 1.5E-5 1/K |
Typical for Chromium Steel |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Chromium Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 440 - 494 J/(kg·K) |
Typical for Chromium Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 23 - 50 W/(m·K) |
Typical for Chromium Steel |
ASTM A752 Grade 5140 Annealed chemical
| Property |
Value |
| Carbon |
Carbon of 0.38 - 0.43 % |
| Chromium |
Chromium of 0.7 - 0.9 % |
| Copper |
Copper of 0.35 % |
| Manganese |
Manganese of 0.7 - 0.9 % |
| Molybdenum |
Molybdenum of 0.06 % |
| Nickel |
Nickel of 0.25 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 0.15 - 0.35 % |
| Sulfur |
Sulfur of 0.04 % |
ASTM A752 Grade 5140 Annealed mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Chromium Steel |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Chromium Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 620 MPa |
- |