EN 10263-4 Grade 41Cr4 quenched and tempered (+QT)
EN 10263-4 Grade 41Cr4 quenched and tempered (+QT) introduction
The cold-upsettable steel 41 Cr 4 can be cold-formed with the suitable tools with a low to medium rate of forming according to the usual forming methods on single-stage and multi-stage presses. It is used for normed screws and screws manufactured according to drawings of strength class 8.8 in the thick dimension range of strength class 12.9 in the thin dimension range. Also used for high-strength parts manufactured according to drawings (ball studs).
Equivalent material: NBN 41Cr4, GB 40CrH, AFNOR 42C4, BS 530M40, GOST 40Ch, ISO C16, UNI 41Cr4KB, JIS SCr440, PN 40H, SS 2245, UNE F.1211-41Cr4DF, ASTM 5140, DIN 1.7035, AFNOR 41Cr4, BS 41Cr4, UNE 41Cr4, AISI 5140, AISI 5140H, SAE 5140, SAE 5140H, JIS SCr440WCH, JIS SCr440H, JIS SCr440M, EN 41Cr4, EN 1.7035, GOST 41H, GOST 38ChA, GB 40Cr, GB/T 40Cr, GB/T A20402, UNS H51400, UNS G51400, IS 40Cr1, IS 40Cr4
EN 10263-4 Grade 41Cr4 quenched and tempered (+QT) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.83 g/cm³ |
EN 10263-4 Grade 41Cr4 quenched and tempered (+QT) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.05E-5 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.15E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.21E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.27E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.32E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.36E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.4E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.44E-5 1/K |
- |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Chromium Steel |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 423 J/(kg·K) |
- |
| - |
20.0 °C |
Specific heat capacity of 461 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 479 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 499 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 517 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 536 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 558 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 587 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 45.1 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 45.1 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 44.1 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 41.9 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 39.4 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 36.9 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 34.4 W/(m·K) |
- |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 12.5 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 11.6 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 10.6 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 9.5 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 8.4 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 7.1 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 5.8 mm²/s |
- |
EN 10263-4 Grade 41Cr4 quenched and tempered (+QT) chemical
| Property |
Value |
| Carbon |
Carbon of 0.38 - 0.45 % |
| Chromium |
Chromium of 0.9 - 1.2 % |
| Manganese |
Manganese of 0.6 - 0.9 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 0.4 % |
| Sulfur |
Sulfur of 0.035 % |
EN 10263-4 Grade 41Cr4 quenched and tempered (+QT) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 2.31E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 2.84E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 3.58E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 4.48E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 5.52E-7 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 6.71E-7 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 8.06E-7 Ω·m |
EN 10263-4 Grade 41Cr4 quenched and tempered (+QT) mechanical
| Property |
Temperature |
Value |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 217 GPa |
| - |
20.0 °C |
Elastic modulus of 212 GPa |
| - |
100.0 °C |
Elastic modulus of 207 GPa |
| - |
200.0 °C |
Elastic modulus of 199 GPa |
| - |
300.0 °C |
Elastic modulus of 192 GPa |
| - |
400.0 °C |
Elastic modulus of 184 GPa |
| - |
500.0 °C |
Elastic modulus of 175 GPa |
| - |
600.0 °C |
Elastic modulus of 164 GPa |
| Elongation |
20.0 °C |
Elongation of 10 - 14 % |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.28 [-] |
| Reduction of area |
20.0 °C |
Reduction of area of 30 - 40 % |
| Tensile strength |
20.0 °C |
Tensile strength of 800 - 1200 MPa |
| Yield strength |
20.0 °C |
Yield strength of 560 - 800 MPa |