ASTM A705 Grade 630 Age-Hardening H1150
Equivalent material: DIN 1.4542, DIN X5CrNiCuNb16-4, DIN X5CrNiCuNb17-4, AFNOR Z7CNU15-05, AFNOR Z7CNU17-04, BS X5CrNiCuNb16-4, AISI 630, AISI 17-4PH, AISI 630 (17-4PH), SAE 630, SAE 17-4PH, SAE 630 (17-4PH), JIS SUS630, JIS SUSF630, JIS SCS24, EN X5CrNiCuNb16-4, EN 1.4542, ISO X5CrNiCuNb16-4, ISO PP20I, ISO 4542-174-00-I, GB 05Cr17Ni4Cu4Nb, ASTM 17-4PH, ASTM CB7Cu-1, ASTM S17400, ASTM Grade F Class 1, UNS S17400
ASTM A705 Grade 630 Age-Hardening H1150 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
Typical for Steel |
ASTM A705 Grade 630 Age-Hardening H1150 chemical
| Property |
Value |
| Carbon |
Carbon of 0.07 % |
| Chromium |
Chromium of 15 - 17.5 % |
| Copper |
Copper of 3 - 5 % |
| Manganese |
Manganese of 1 % |
| Nickel |
Nickel of 3 - 5 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.03 % |
ASTM A705 Grade 630 Age-Hardening H1150 mechanical
| Property |
Temperature |
Value |
Comment |
| Charpy impact energy |
23.0 °C |
Charpy impact energy of 41 J |
- |
| Elastic modulus |
23.0 °C |
Elastic modulus of 190 - 210 GPa |
Typical for Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 16 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 277 [-] |
- |
| Hardness, Rockwell C |
23.0 °C |
Hardness, Rockwell C of 28 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 50 % |
- |
| Tensile strength |
23.0 °C |
Tensile strength of 930 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 725 MPa |
- |