ASTM A508 Grade 6 Class 1, Quenched and Tempered
Equivalent material: AISI 410, SAE 410, JIS SUS410, ASTM Grade 6, UNS S41000
ASTM A508 Grade 6 Class 1, Quenched and Tempered general
| Property |
Temperature |
Value |
Comment |
| Density |
20.0 °C |
Density of 7.6 - 7.7 g/cm³ |
Typical for Martensitic Stainless Steel |
ASTM A508 Grade 6 Class 1, Quenched and Tempered thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
20.0 °C |
Coefficient of thermal expansion of 1E-5 - 1.5E-5 1/K |
Typical for Martensitic Stainless Steel |
| Melting point |
- |
Melting point of 1375 - 1450 °C |
Typical for Martensitic Stainless Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 460 J/(kg·K) |
Typical for Martensitic Stainless Steel |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 14 - 31 W/(m·K) |
Typical for Martensitic Stainless Steel |
ASTM A508 Grade 6 Class 1, Quenched and Tempered chemical
| Property |
Value |
| Aluminium |
Aluminium of 0.03 % |
| Boron |
Boron of 3E-3 % |
| Calcium |
Calcium of 0.02 % |
| Carbon |
Carbon of 0.28 - 0.33 % |
| Chromium |
Chromium of 0.7 - 1 % |
| Copper |
Copper of 0.25 % |
| Manganese |
Manganese of 0.75 - 1.15 % |
| Molybdenum |
Molybdenum of 0.3 - 0.45 % |
| Nickel |
Nickel of 0.75 - 0.95 % |
| Niobium |
Niobium of 0.01 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.35 % |
| Sulfur |
Sulfur of 0.025 % |
| Titanium |
Titanium of 0.02 % |
| Vanadium |
Vanadium of 0.05 % |
ASTM A508 Grade 6 Class 1, Quenched and Tempered electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 6E-7 Ω·m |
Typical for Martensitic Stainless Steel |
ASTM A508 Grade 6 Class 1, Quenched and Tempered mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 220 GPa |
Typical for Martensitic Stainless Steel |
| Elongation A50 |
20.0 °C |
Elongation A50 of 20 % |
- |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Martensitic Stainless Steel |
| Reduction of area |
20.0 °C |
Reduction of area of 35 % |
- |
| Tensile strength |
20.0 °C |
Tensile strength of 585 - 760 MPa |
- |
| Yield Strength Rp0.2, short transverse |
20.0 °C |
Yield Strength Rp0.2, short transverse of 415 MPa |
- |
From fabrication to delivery, we ensure excellence in every aspect of our steel products.
-- Our promise