ASTM A463 Grade DDS Aluminum-Coated by the Hot-Dip Process
Equivalent material: DIN 1.0306, DIN St 06 Z, DIN DX54D, AFNOR DX54D, BS DX54D, UNI FeP06G, JIS SGCD1, JIS SGCD3, JIS SGCMD3, JIS SZACD3, JIS SZACD4, EN DX54D, EN 1.0306, ISO 05, GOST 05, GB/T DX54D
ASTM A463 Grade DDS Aluminum-Coated by the Hot-Dip Process general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
ASTM A463 Grade DDS Aluminum-Coated by the Hot-Dip Process thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
ASTM A463 Grade DDS Aluminum-Coated by the Hot-Dip Process chemical
| Property |
Value |
| Aluminium |
Aluminium of 0.01 % |
| Carbon |
Carbon of 0.06 % |
| Chromium |
Chromium of 0.15 % |
| Copper |
Copper of 0.2 % |
| Manganese |
Manganese of 0.5 % |
| Molybdenum |
Molybdenum of 0.06 % |
| Nickel |
Nickel of 0.2 % |
| Niobium |
Niobium of 8E-3 % |
| Phosphorus |
Phosphorus of 0.02 % |
| Sulfur |
Sulfur of 0.025 % |
| Titanium |
Titanium of 0.3 % |
| Vanadium |
Vanadium of 8E-3 % |
ASTM A463 Grade DDS Aluminum-Coated by the Hot-Dip Process magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
ASTM A463 Grade DDS Aluminum-Coated by the Hot-Dip Process electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
ASTM A463 Grade DDS Aluminum-Coated by the Hot-Dip Process mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 32 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Yield strength |
23.0 °C |
Yield strength of 140 - 240 MPa |
- |
Experience the strength, resilience, and versatility of our premium steel products.
-- Our promise