ASTM A1008 Grade EDDS
Equivalent material: DIN 1.0873, DIN IF 18, DIN FeP06, DIN DC06, AFNOR DC06, AFNOR IF, BS DC06, JIS SPCG, JIS SECG, EN DC06, EN HX260YD, EN 1.0873, ISO CR5, ISO T005, ISO 05, GB/T LT05, GB/T U43016, GB/T DC06
ASTM A1008 Grade EDDS general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
ASTM A1008 Grade EDDS thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
ASTM A1008 Grade EDDS chemical
| Property |
Value |
| Aluminium |
Aluminium of 0.01 % |
| Carbon |
Carbon of 0.02 % |
| Chromium |
Chromium of 0.15 % |
| Copper |
Copper of 0.1 % |
| Manganese |
Manganese of 0.4 % |
| Molybdenum |
Molybdenum of 0.03 % |
| Nickel |
Nickel of 0.1 % |
| Niobium |
Niobium of 0.1 % |
| Phosphorus |
Phosphorus of 0.02 % |
| Sulfur |
Sulfur of 0.02 % |
| Titanium |
Titanium of 0.15 % |
| Vanadium |
Vanadium of 0.1 % |
ASTM A1008 Grade EDDS magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
ASTM A1008 Grade EDDS electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
ASTM A1008 Grade EDDS mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 40 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Yield strength |
23.0 °C |
Yield strength of 105 - 170 MPa |
- |