ASTM A295 Grade 1070M Annealed, Cold-Drawn
Equivalent material: DIN 1.0603, DIN C67, AFNOR C68, BS 70CS, BS 70HS, JIS SWRH72B, JIS S70C-CSP, EN 1.0603, ISO CS70, GOST 70, ASTM Grade 1070M, DIN 1.0615, DIN D 70-2, DIN C70D, AFNOR C70D, BS C70D, AISI 1070, SAE 1070, EN C70D, EN 1.0615, ISO C70D, GOST 3K-7, GB 70, GB U20702, GB/T 70, GB/T U20702, GB/T C70D, GB/T U53702, GB/T U59702, UNS G10700, DIN 1.1231, DIN Ck67, DIN C67S, AFNOR C68RR, AFNOR XC68, AFNOR C67S, BS C67S, UNI C70, JIS S70CM, JIS S70C, EN C67S, EN 1.1231, ISO CS65, GOST 65G, GOST 65GA, GOST 65, GB 65, GB U20652, GB/T 65, GB/T U20652, ASTM 1070, IS C70, DIN 1.1248, DIN Ck75, DIN C75S, AFNOR C75S, AFNOR C75RR, AFNOR XC75, BS 060A78, BS C75S, BS CS70, BS 80, AISI 1075, AISI 1078, AISI 1074, SAE 1075, SAE 1078, SAE 1074, JIS S75CM, JIS SWRH77B, EN C75S, EN 1.1248, ISO CS75, GOST 75, GOST 75A, GB/T 75, GB/T U20752, ASTM Grade 1074, UNS G10750, UNS G10780, UNS G10740, DIN 1.1244, DIN 70Mn4, AFNOR 70Mn4, BS 70Mn4, JIS 70Mn4, EN 1.1244, ISO 70Mn4, ISO B42, GB/T 70Mn, GB/T U21702, DIN 1.9613, DIN SAE 1070, EN 1.9613
ASTM A295 Grade 1070M Annealed, Cold-Drawn general
| Property |
Temperature |
Value |
Comment |
| Density |
20.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for High Carbon Steel |
ASTM A295 Grade 1070M Annealed, Cold-Drawn thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
20.0 °C |
Coefficient of thermal expansion of 1.32E-5 1/K |
Typical for High Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1289 - 1478 °C |
Typical for High Carbon Steel |
ASTM A295 Grade 1070M Annealed, Cold-Drawn chemical
| Property |
Value |
| Aluminium |
Aluminium of 0.05 % |
| Carbon |
Carbon of 0.65 - 0.75 % |
| Chromium |
Chromium of 0.2 % |
| Copper |
Copper of 0.3 % |
| Manganese |
Manganese of 0.8 - 1.1 % |
| Molybdenum |
Molybdenum of 0.1 % |
| Nickel |
Nickel of 0.25 % |
| Oxygen |
Oxygen of 1.5E-3 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.15 - 0.35 % |
| Sulfur |
Sulfur of 0.015 % |
ASTM A295 Grade 1070M Annealed, Cold-Drawn electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
ASTM A295 Grade 1070M Annealed, Cold-Drawn mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for High Carbon Steel |
| Hardness, Brinell |
20.0 °C |
Hardness, Brinell of 248 [-] |
- |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for High Carbon Steel |
| Shear modulus |
20.0 °C |
Shear modulus of 75 - 80 GPa |
Typical for Carbon Steel |