ASTM A1011 SS Grade 250 Type 2
Equivalent material: DIN 1.0038, DIN RSt 37-2, DIN S235JRG2, AFNOR S235JR, BS S235JR, JIS SS330, JIS SNR400, JIS STKM12A, JIS STKM12C, JIS SNR400A, JIS SNR400B, JIS SNR490B, EN S235JR, EN 1.0038, ISO HR235-D, GOST St3ps, GOST St3ks, GOST St3sp, GB/T CRB650, GB/T Q235, ASTM Grade 1, ASTM SS Grade 250 Type 1, UNS K03000, UNS K01500, DIN 1.0114, DIN St 37-3 U, DIN S235J0, AFNOR E 24-3, AFNOR S235J0, BS 40C, BS S235J0, AISI 1011, SAE 1011, JIS E235C, EN S235J0, EN 1.0114, ISO S235C, GOST St3Gsp, GB/T Q235C, GB/T U12358, UNS K02401
ASTM A1011 SS Grade 250 Type 2 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
ASTM A1011 SS Grade 250 Type 2 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
ASTM A1011 SS Grade 250 Type 2 chemical
| Property |
Value |
| Carbon |
Carbon of 0.25 % |
| Chromium |
Chromium of 0.15 % |
| Copper |
Copper of 0.2 % |
| Manganese |
Manganese of 1.35 % |
| Molybdenum |
Molybdenum of 0.06 % |
| Nickel |
Nickel of 0.2 % |
| Niobium |
Niobium of 8E-3 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Sulfur |
Sulfur of 0.04 % |
| Titanium |
Titanium of 0.03 % |
| Vanadium |
Vanadium of 8E-3 % |
ASTM A1011 SS Grade 250 Type 2 magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
ASTM A1011 SS Grade 250 Type 2 electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
ASTM A1011 SS Grade 250 Type 2 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation A200 |
23.0 °C |
Elongation A200 of 16 % |
- |
| Elongation A50 |
23.0 °C |
Elongation A50 of 16 - 21 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 400 - 550 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 250 MPa |
- |