AISI 420F Annealed

AISI 420F Annealed

Equivalent material: DIN 1.4028, DIN X30Cr13, AFNOR Z33C13, BS 420S45, SAE 420F, JIS SUS420J2, JIS SUS420J2FB, JIS SUS420J2TKA, EN X30Cr13, EN 1.4028, ISO 30Cr13, GOST 30Ch13, GB 3Cr13, ASTM 420F, UNS S42000, DIN 1.4029, AFNOR Z30CF13, JIS SUS420F, EN X29CrS13, EN 1.4029, UNS S42020

AISI 420F Annealed general

Property Temperature Value
Density 23.0 °C Density of 7.8 g/cm³

AISI 420F Annealed thermal

Property Temperature Value Comment
Coefficient of thermal expansion 23.0 °C Coefficient of thermal expansion of 1.2E-5 1/K -
Melting point - Melting point of 1370 - 1530 °C Typical for Martensitic Stainless Steel
Specific heat capacity 23.0 °C Specific heat capacity of 460 J/(kg·K) -
Thermal conductivity 23.0 °C Thermal conductivity of 28 W/(m·K) -

AISI 420F Annealed chemical

Property Value
Carbon Carbon of 0.26 - 0.42 %
Chromium Chromium of 12 - 14.5 %
Iron Iron of 82.4 - 87.7 %
Manganese Manganese of 0 - 1.5 %
Molybdenum Molybdenum of 0 - 0.5 %
Phosphorus Phosphorus of 0 - 0.06 %
Silicon Silicon of 0 - 1 %
Sulfur Sulfur of 0 - 0.35 %

AISI 420F Annealed electrical

Property Temperature Value Comment
Electrical resistivity 23.0 °C Electrical resistivity of 6E-7 Ω·m Typical for Martensitic Stainless Steel

AISI 420F Annealed mechanical

Property Temperature Value Comment
Elastic modulus 23.0 °C Elastic modulus of 210 GPa -
Elongation 23.0 °C Elongation of 16 % -
Poisson's ratio 23.0 °C Poisson's ratio of 0.3 [-] Typical for Martensitic Stainless Steel
Shear modulus 23.0 °C Shear modulus of 77 GPa Typical for Martensitic Stainless Steel
Tensile strength 23.0 °C Tensile strength of 640 MPa -
Yield strength 23.0 °C Yield strength of 400 MPa -