AISI 321H Annealed
Equivalent material: DIN 1.4941, DIN X8CrNiTi18-10, DIN X6CrNiTiB18-10, DIN X7CrNiTiB18-10, AFNOR Z6CNT18-10, SAE 321H, EN X6CrNiTiB18-10, EN X7CrNiTiB18-10, EN 1.4941, UNS S32109
AISI 321H Annealed general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
AISI 321H Annealed thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.3E-5 1/K |
- |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 450 J/(kg·K) |
- |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 11 - 21 W/(m·K) |
Typical for Austenitic Stainless Steel |
AISI 321H Annealed chemical
| Property |
Value |
| Boron |
Boron of 1.5E-3 - 5E-3 % |
| Carbon |
Carbon of 0.04 - 0.1 % |
| Chromium |
Chromium of 17 - 19 % |
| Iron |
Iron of 64 - 74 % |
| Manganese |
Manganese of 0 - 2 % |
| Nickel |
Nickel of 9 - 13 % |
| Nitrogen |
Nitrogen of 0 - 0.1 % |
| Phosphorus |
Phosphorus of 0 - 0.05 % |
| Silicon |
Silicon of 0 - 1 % |
| Sulfur |
Sulfur of 0 - 0.03 % |
| Titanium |
Titanium of 0 - 0.8 % |
AISI 321H Annealed electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
AISI 321H Annealed mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 220 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 35 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 590 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 240 MPa |
- |