AISI 310 Hot Finished
Equivalent material: SAE 310, ASTM TP310, ASTM 310, UNS S31000
AISI 310 Hot Finished general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.9 g/cm³ |
AISI 310 Hot Finished thermal
| Property |
Temperature |
Value |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.5E-5 1/K |
| Melting point |
- |
Melting point of 1400 °C |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 500 J/(kg·K) |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 15 W/(m·K) |
AISI 310 Hot Finished chemical
| Property |
Value |
| Carbon |
Carbon of 0 - 0.25 % |
| Chromium |
Chromium of 24 - 26 % |
| Iron |
Iron of 48.2 - 57 % |
| Manganese |
Manganese of 0 - 2 % |
| Nickel |
Nickel of 19 - 22 % |
| Nitrogen |
Nitrogen of 0 - 0.1 % |
| Phosphorus |
Phosphorus of 0 - 0.05 % |
| Silicon |
Silicon of 0 - 1.5 % |
| Sulfur |
Sulfur of 0 - 0.03 % |
AISI 310 Hot Finished electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
AISI 310 Hot Finished mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 46 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 600 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 260 MPa |
- |