JIS G4312 Grade SUH310 solution treated
Equivalent material: GB/T 1Cr25Ni20Si2, GB/T 2Cr25Ni20, GB 2Cr25Ni20, GOST Ch25N20L, AS 2837, AS 310, DIN X15CrNiSi2520, NF Z12CN25-20, BS 310S24, BS 310S31, UNI X22CrNi2520, UNI X16CrNiSi2520, EN X15CrNiSi25-21, UNE X15CrNiSi25-20, SIS 2361-02, SIS 2376, ASME 310, ASTM 310, ASTM F310, ASTM TP310, MIL 310, JIS SUS310STB, JIS SUS310STP, JIS SUSF310, JIS SUSY310, AISI 310, GOST 20H25N19S2L, AMS 5652, AMS 5522, AMS 7490, ASTM 314, AISI 314, EN GX2CrNiMoN25-7-3, EN X2CrNiMoSi18-5-3, ASTM S31500, AISI S31500, DIN 1.4841, DIN X15CrNiSi25-20, DIN X15CrNiSi25-21, SAE 314, JIS SUS310TP, JIS SUS310TB, JIS SUS310TF, EN 1.4841, GOST 20Ch25N20S2, GB 1Cr25Ni20Si2, UNS S31400, IS X20Cr2Ni20, DIN 1.4845, DIN X12CrNi25-21, DIN X8CrNi25-21, AFNOR Z12CN2520, UNI X6CrNi2520, SS 2361, UNE F.331, AISI 310S, SAE 310S, JIS SUS310S, JIS SUS310STPY, JIS SUS310SFB, EN X8CrNi25-21, EN 1.4845, UNS S31008
JIS G4312 Grade SUH310 solution treated general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.9 - 8.2 g/cm³ |
Typical for Austenitic Stainless Steel |
JIS G4312 Grade SUH310 solution treated thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K |
Typical for Austenitic Stainless Steel |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 440 J/(kg·K) |
Typical for Austenitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 11 - 21 W/(m·K) |
Typical for Austenitic Stainless Steel |
JIS G4312 Grade SUH310 solution treated electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
JIS G4312 Grade SUH310 solution treated mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 35 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 201 [-] |
- |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 95 [-] |
- |
| Hardness, Vickers |
23.0 °C |
Hardness, Vickers of 210 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 590 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 205 MPa |
- |