AISI 309 Hot Finished
Equivalent material: DIN 1.4828, DIN X15CrNiSi2012, DIN X15CrNiSi20-12, AFNOR Z15CNS20.12, AFNOR Z9CN24-13, BS 309S24, SAE 309, JIS SUH309, JIS SUS309TP, JIS SUS309TB, JIS SUS309TF, EN X15CrNiSi20-12, EN 1.4828, GOST 20Ch20N14S2, UNS S30900
AISI 309 Hot Finished general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
AISI 309 Hot Finished thermal
| Property |
Temperature |
Value |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.5E-5 1/K |
| Melting point |
- |
Melting point of 1400 °C |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 500 J/(kg·K) |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 16 W/(m·K) |
AISI 309 Hot Finished chemical
| Property |
Value |
| Carbon |
Carbon of 0 - 0.2 % |
| Chromium |
Chromium of 19 - 24 % |
| Iron |
Iron of 58 - 68.5 % |
| Manganese |
Manganese of 0 - 2 % |
| Nickel |
Nickel of 11 - 15 % |
| Nitrogen |
Nitrogen of 0 - 0.1 % |
| Phosphorus |
Phosphorus of 0 - 0.05 % |
| Silicon |
Silicon of 0 - 2.5 % |
| Sulfur |
Sulfur of 0 - 0.03 % |
AISI 309 Hot Finished electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
AISI 309 Hot Finished mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 48 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 610 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 260 MPa |
- |