JIS G4311 Grade SUH309 solution treated
Equivalent material: GB/T 1Cr20Ni14Si2, GB 2Cr23Ni13, GOST 20Х20Н14С2, GOST 20H20N14S2, NF Z9CN24-13, BS 309S24, UNI X16CrNi2314, EN X15CrNiSi20-12, UNE X15CrNiSi20-12, ASME 309, ASTM 308, ASTM 309, ASTM CR309, ASTM WP309, MIL 309, JIS SUS309STB, JIS SUS309STP, AISI 309, AISI 309S, SAE 309S, ASTM TP309S, ASTM 309S, UNS S30908, ASTM MT309S, DIN 1.4828, DIN X15CrNiSi2012, DIN X15CrNiSi20-12, AFNOR Z15CNS20.12, AFNOR Z9CN24-13, SAE 309, JIS SUS309TP, JIS SUS309TB, JIS SUS309TF, EN 1.4828, GOST 20Ch20N14S2, UNS S30900
JIS G4311 Grade SUH309 solution treated general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.9 - 8.2 g/cm³ |
Typical for Austenitic Stainless Steel |
JIS G4311 Grade SUH309 solution treated thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K |
Typical for Austenitic Stainless Steel |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 440 J/(kg·K) |
Typical for Austenitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 11 - 21 W/(m·K) |
Typical for Austenitic Stainless Steel |
JIS G4311 Grade SUH309 solution treated electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
JIS G4311 Grade SUH309 solution treated mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 45 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 201 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 50 % |
- |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 560 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 205 MPa |
- |