JIS G4304 Grade SUS309S solution treated
Equivalent material: GB/T 0Cr23Ni13, GB/T 0Cr23Ni13-R, GB 0Cr23Ni13, NF Z15CN24-13, NF Z20CN24-13, UNI X6CrNi2314, EN X12CrNi23-13, ASTM CH8, ASTM CPH8, NF Z10CN24-13, AMS 5523, AMS 5574, AMS 5650, AMS 7490, ASME 309S, ASTM TP309S, ASTM 309S, ASTM MT309S, AISI 309S, SAE 309S, DIN 1.4950, EN X6CrNi23-13, EN 1.4950, UNS S30908, DIN 1.4833, DIN X7CrNi23-14, AFNOR Z20CN24-13, JIS SUS309STP, JIS SUS309STPY, JIS SUS309STB, EN X7CrNi23-14, EN 1.4833
JIS G4304 Grade SUS309S solution treated general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.9 - 8.2 g/cm³ |
Typical for Austenitic Stainless Steel |
JIS G4304 Grade SUS309S solution treated thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K |
Typical for Austenitic Stainless Steel |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 440 J/(kg·K) |
Typical for Austenitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 11 - 21 W/(m·K) |
Typical for Austenitic Stainless Steel |
JIS G4304 Grade SUS309S solution treated electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
JIS G4304 Grade SUS309S solution treated mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 40 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 187 [-] |
- |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 90 [-] |
- |
| Hardness, Vickers |
23.0 °C |
Hardness, Vickers of 200 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 520 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 205 MPa |
- |