AISI 1060 Hot Rolled
Equivalent material: DIN 1.0601, DIN C60, AFNOR CC55, AFNOR C60, BS 080A62, BS 60CS, BS 60HS, BS En9, BS 070M55, BS C60, BS 060A62, UNI C60, SAE 1060, JIS S60C, JIS S58C, JIS SWRH62B, JIS S65C, EN C60, EN 1.0601, ISO C60, ISO CS60, GOST 2, GOST 60, GOST 60G, GB/T 60, GB/T CRB970, GB/T U20602, ASTM 1060, UNS G10600, DIN 1.0609, DIN D 58-2, DIN C58D, AFNOR C58D, BS C58D, JIS SWRH57, JIS SWRH57A, JIS CS55, EN C58D, EN 1.0609, ISO C58D, GB/T C58D, GB/T U53582, DIN 1.0610, DIN D 60-2, DIN C60D, AFNOR C60D, BS C60D, JIS CS60, EN C60D, EN 1.0610, ISO C60D, GB/T C60D, GB/T U53602, DIN 1.1223, DIN Cm 60, DIN Cm60, DIN C60R, AFNOR C60R, BS C60R, EN C60R, EN 1.1223, ISO C60R, ISO C60M2
AISI 1060 Hot Rolled general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
AISI 1060 Hot Rolled thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.2E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1289 - 1478 °C |
Typical for High Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 450 J/(kg·K) |
- |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 36 W/(m·K) |
Typical for High Carbon Steel |
AISI 1060 Hot Rolled chemical
| Property |
Value |
| Carbon |
Carbon of 0.55 - 0.65 % |
| Iron |
Iron of 98.4 - 98.9 % |
| Manganese |
Manganese of 0.6 - 0.9 % |
| Phosphorus |
Phosphorus of 0 - 0.04 % |
| Sulfur |
Sulfur of 0 - 0.05 % |
AISI 1060 Hot Rolled electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
AISI 1060 Hot Rolled mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 210 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 13 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for High Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 81 GPa |
Typical for High Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 730 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 400 MPa |
- |
Experience the unmatched durability and longevity of our steel materials.