UGIMA® 4570 Annealed
UGIMA® 4570 Annealed introduction
UGIMA® 4570 is an improved machinability stainless steel manufactured only by UGITECH. Its properties are identical to those of 303, except for its machinability, which is even better.
The SULPHUR + COPPER + UGIMA® Process synergy achieves previously unimaginable, but now unrivalled machining performances: cutting speed up to 750 m/min during turning with a coated carbide insert.
Similarly, this synergy provides improved chip breakability and tool life and increases productivity by up to 70% over 1.4305 (303) and 20% over UGIMA® 4305.
The addition of copper reduces sensitivity to cold work-hardening compared with 1.4305 and improves machining operations such as knurling, deep drilling, threading and tapping by rolling, as well as bending and crimping (door and cupboard handles).
Austenitic, therefore non-magnetic grade after annealing at 1000/1100°C (magnetic permeability µ
Equivalent material: EN 1.4570, EN X8CrNiCuS18-9-2, DIN 1.4570, DIN X8CrNiCuS18-9-2, JIS SUS303Cu
UGIMA® 4570 Annealed general
| Property |
Value |
| Density |
Density of 7.9 g/cm³ |
UGIMA® 4570 Annealed thermal
| Property |
Value |
Comment |
| Coefficient of thermal expansion |
Coefficient of thermal expansion of 0.0000165 1/K |
20 to 200°C |
| Thermal conductivity |
Thermal conductivity of 16.7 W/(m·K) |
- |
UGIMA® 4570 Annealed chemical
| Property |
Value |
Comment |
| Carbon |
Carbon of 0.04 - 0.08 % |
- |
| Chromium |
Chromium of 17.0 - 18.0 % |
- |
| Copper |
Copper of 1.4 - 1.8 % |
- |
| Manganese |
Manganese of 1.5 - 2.0 % |
- |
| Molybdenum |
Molybdenum of 0.5 |
max. |
| Nickel |
Nickel of 8.0 - 9.0 % |
- |
| Phosphorus |
Phosphorus of 0.04 |
max. |
| Silicon |
Silicon of 0.75 |
max. |
| Sulfur |
Sulfur of 0.25 - 0.35000000000000003 % |
- |
UGIMA® 4570 Annealed magnetic
| Property |
Value |
Comment |
| Relative magnetic permeability |
Relative magnetic permeability of 1.03 [-] |
max. |
UGIMA® 4570 Annealed electrical
| Property |
Value |
| Electrical resistivity |
Electrical resistivity of 7e-07 Ω·m |
UGIMA® 4570 Annealed mechanical
| Property |
Value |
| Elastic modulus |
Elastic modulus of 193 GPa |
| Elongation |
Elongation of 55.0 - 60.0 % |
| Reduction of area |
Reduction of area of 60.0 - 65.0 % |
| Tensile strength |
Tensile strength of 570.0 - 620.0 MPa |
Our steel is the foundation for safe and reliable infrastructure projects.