UGIMA® 4541 Work Hardened (drawn)
UGIMA® 4541 Work Hardened (drawn) introduction
The main property of UGIMA® 4541 is its resistance to intergranular corrosion. It uses titanium as a stabilising element to avoid the formation of chromium carbides in the grade when it is used at high temperature.
The mechanical properties of this stainless steel are better than those of 1.4307.
UGIMA® 4541 is specifically designed for machining and bar turning and provides increased productivity for these operations.
UGIMA® 4541 has excellent oxidation and corrosion resistance and good creep behaviour. It is particularly recommended for applications requiring heat resistance at continuous or cyclic operating temperatures (400 – 850°C).
Equivalent material: DIN 1.4541, DIN X6CrNiTi18-10, UNS S32100, AISI 321, JIS SUS321, ISO 4541-321-00-I, ISO X6CrNiTi18-10, EN 1.4541, EN X6CrNiTi18-10
UGIMA® 4541 Work Hardened (drawn) general
| Property |
Value |
| Density |
Density of 7.9 g/cm³ |
UGIMA® 4541 Work Hardened (drawn) thermal
| Property |
Value |
Comment |
| Coefficient of thermal expansion |
Coefficient of thermal expansion of 0.000016 1/K |
20 to 100°C |
| - |
Coefficient of thermal expansion of 0.0000165 1/K |
20 to 200°C |
| - |
Coefficient of thermal expansion of 0.000017 1/K |
20 to 300°C |
| - |
Coefficient of thermal expansion of 0.0000175 1/K |
20 to 400°C |
| - |
Coefficient of thermal expansion of 0.000018 1/K |
20 to 500°C |
| Specific heat capacity |
Specific heat capacity of 500 J/(kg·K) |
- |
| Thermal conductivity |
Thermal conductivity of 15 W/(m·K) |
- |
UGIMA® 4541 Work Hardened (drawn) chemical
| Property |
Value |
Comment |
| Carbon |
Carbon of 0.08 |
max. |
| Chromium |
Chromium of 17.0 - 19.0 % |
- |
| Manganese |
Manganese of 2.0 |
max. |
| Molybdenum |
Molybdenum of 0.5 |
max. |
| Nickel |
Nickel of 9.0 - 12.0 % |
- |
| Phosphorus |
Phosphorus of 0.045 |
max. |
| Silicon |
Silicon of 1.0 |
max. |
| Sulfur |
Sulfur of 0.03 |
max. |
| Titanium |
Titanium of 0.7000000000000001 |
max., min: 5x(C+N) |
UGIMA® 4541 Work Hardened (drawn) electrical
| Property |
Value |
| Electrical resistivity |
Electrical resistivity of 7.3e-07 Ω·m |
UGIMA® 4541 Work Hardened (drawn) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20 °C |
Elastic modulus of 200 GPa |
- |
| - |
100 °C |
Elastic modulus of 194 GPa |
- |
| - |
200 °C |
Elastic modulus of 186 GPa |
- |
| - |
300 °C |
Elastic modulus of 180 GPa |
- |
| - |
400 °C |
Elastic modulus of 172 GPa |
- |
| - |
500 °C |
Elastic modulus of 165 GPa |
- |
| Elongation |
- |
Elongation of 25.0 - 30.0 % |
min., depending on the size |
| Tensile strength |
- |
Tensile strength of 500.0 - 950.0 MPa |
min., depending on the size |
UGIMA® 4541 Work Hardened (drawn) application
| Property |
- |
- |
| Application areas |
| Corrosion properties |
Oxidizing atmosphere |
850°C |
| Oxidizing sulphur atmosphere |
750°C |
Our steel products are engineered to deliver long-lasting performance, offering an excellent return on investment.
-- Our promise