UGICHROM® 4462
UGICHROM® 4462 introduction
UGICHROM® is the result of combining the high efficiency of micro-fissuring chromium plating with the technology of the most advanced stainless steel bars. The UGICHROM® product range is recommended for hydraulic and pneumatic mechanisms.
General properties - choice for performance:
Low friction coefficient.
High resistance to wear.
Increased corrosion resistance.
Micro-fissuring chromium plating guarantees excellent performance under extreme conditions of service.
Improved machinability (up to +20% of productivity).
High mechanical properties.
Accurate geometrical and dimensional properties..
Equivalent material: EN 1.4462, EN X2CrNiMoN22-5-3, DIN 1.4462, DIN X2CrNiMoN22-5-3, AISI F51
UGICHROM® 4462 general
| Property |
Value |
| Density |
Density of 7.8 g/cm³ |
UGICHROM® 4462 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
- |
Coefficient of thermal expansion of 0.000013 1/K |
20 to 100°C |
| - |
- |
Coefficient of thermal expansion of 0.0000135 1/K |
20 to 200°C |
| - |
- |
Coefficient of thermal expansion of 0.000014 1/K |
20 to 300°C |
| Specific heat capacity |
20 °C |
Specific heat capacity of 500 J/(kg·K) |
- |
| - |
100 °C |
Specific heat capacity of 530 J/(kg·K) |
- |
| - |
200 °C |
Specific heat capacity of 560 J/(kg·K) |
- |
| - |
300 °C |
Specific heat capacity of 590 J/(kg·K) |
- |
| Thermal conductivity |
20 °C |
Thermal conductivity of 15 W/(m·K) |
- |
| - |
100 °C |
Thermal conductivity of 16 W/(m·K) |
- |
| - |
200 °C |
Thermal conductivity of 17 W/(m·K) |
- |
| - |
300 °C |
Thermal conductivity of 18 W/(m·K) |
- |
UGICHROM® 4462 chemical
| Property |
Value |
Comment |
| Carbon |
Carbon of 0.03 |
max. |
| Chromium |
Chromium of 22.0 - 23.0 % |
- |
| Manganese |
Manganese of 1.0 - 2.0 % |
- |
| Molybdenum |
Molybdenum of 2.5 - 3.5 % |
- |
| Nickel |
Nickel of 5.0 - 6.0 % |
- |
| Nitrogen |
Nitrogen of 0.12 - 0.2 % |
- |
| Phosphorus |
Phosphorus of 0.035 |
max. |
| Silicon |
Silicon of 0.75 |
max. |
| Sulfur |
Sulfur of 0.01 % |
max. |
UGICHROM® 4462 electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20 °C |
Electrical resistivity of 0.0000008 Ω·m |
| - |
100 °C |
Electrical resistivity of 0.00000085 Ω·m |
| - |
200 °C |
Electrical resistivity of 0.0000009 Ω·m |
| - |
300 °C |
Electrical resistivity of 0.000001 Ω·m |
UGICHROM® 4462 mechanical
| Property |
Temperature |
Value |
| Elastic modulus |
20 °C |
Elastic modulus of 200 GPa |
| - |
100 °C |
Elastic modulus of 194 GPa |
| - |
200 °C |
Elastic modulus of 186 GPa |
| - |
300 °C |
Elastic modulus of 180 GPa |
| Tensile strength |
- |
Tensile strength of 650.0 - 880.0 MPa |
UGICHROM® 4462 application
| Property |
- |
- |
| Application areas |
| Corrosion properties |
| Other |
CHARACTERISTICS |
Standard product |
Special product |
| Diameter tolerance |
ISO f7 |
On request |
| Bar length dia. 12 to 19 mm |
2900 mm +200/-0 |
On request |
| Bar length dia. 20 to 125 mm |
6000 mm +/- 500 mm |
On request |
| Roundness |
<1/2 f7 ISO |
- |
| Straightness (to EN 10278) |
<0.5 mm/ml |
Up to 0.2 mm for dia. >30 mm |
| Roughness |
Ra < 0.2 µm |
Up to Ra <0.08 µm |
| Chromium structure |
Microcracked |
- |
| Sizes |
Dia. 12 to 125 mm |
On request |
| Thickness of the chromium dia. 12 to 19.5 mm |
18 µm +/-3 |
Max. 50 µm |
| Thickness of the chromium dia. 20 to 115 mm |
25 µm +/-5 |
Max. 100 µm |