UGI® HT286 Annealed and Cold Drawn and Aged
UGI® HT286 Annealed and Cold Drawn and Aged introduction
UGI® HT286 is an austenitic iron-base alloy containing nickel, chromium, molybdenum and titanium. The titanium and small amount of aluminium it contains enables the alloy to be strengthened by precipitation of the Ni3 (Ti,Al) gamma prime phase, providing good mechanical properties from cryogenic temperatures up to 700°C.
Equivalent material: EN 1.4980, EN 1.4944, DIN 1.4980, DIN 1.4944, UNS S66286, AISI 660
UGI® HT286 Annealed and Cold Drawn and Aged general
| Property |
Value |
| Density |
Density of 8 g/cm³ |
UGI® HT286 Annealed and Cold Drawn and Aged thermal
| Property |
Value |
Comment |
| Coefficient of thermal expansion |
Coefficient of thermal expansion of 0.0000165 1/K |
20 to 100°C |
| Melting point |
Melting point of 1370.0 - 1400.0 °C |
- |
| Thermal conductivity |
Thermal conductivity of 14 W/(m·K) |
- |
UGI® HT286 Annealed and Cold Drawn and Aged chemical
| Property |
Value |
Comment |
| Aluminium |
Aluminium of 0.35000000000000003 |
max. |
| Boron |
Boron of 0.03 - 0.1 % |
- |
| Carbon |
Carbon of 0.08 |
max. |
| Chromium |
Chromium of 13.5 - 16.0 % |
- |
| Manganese |
Manganese of 1.0 - 2.0 % |
- |
| Molybdenum |
Molybdenum of 1.0 - 1.5 % |
- |
| Nickel |
Nickel of 24.0 - 27.0 % |
- |
| Phosphorus |
Phosphorus of 0.025 |
max. |
| Silicon |
Silicon of 1.0 |
max. |
| Sulfur |
Sulfur of 0.015 % |
min. |
| Titanium |
Titanium of 1.9 - 2.3 % |
- |
| Vanadium |
Vanadium of 0.1 - 0.5 % |
- |
UGI® HT286 Annealed and Cold Drawn and Aged electrical
| Property |
Value |
| Electrical resistivity |
Electrical resistivity of 9.1e-07 Ω·m |
UGI® HT286 Annealed and Cold Drawn and Aged mechanical
| Property |
Value |
Comment |
| Elongation |
Elongation of 12 % |
min. |
| Tensile strength |
Tensile strength of 1103 MPa |
min. |
| Yield strength |
Yield strength of 827 MPa |
min. |
UGI® HT286 Annealed and Cold Drawn and Aged application
| Property |
- |
- |
| Application areas |
| Corrosion properties |
Environment |
Behaviour |
| Sea water |
Moderate |
| Humidity |
Excellent |
| Sour oil/gas |
Moderate |
| Salt spray (NaCl) |
Good |