JIS G4311 Grade SUH660 ageing treatment after solution treatment
Equivalent material: S-Liste X6NiCrTi2615, NF Z6NCTDV25-15, NF Z5NCTDV25-15B, NF Z6NCTDV25-15B, NF Z8NCTDV25-15BFF, BS HR51, BS 286S31, AMS 5726, AMS 5731, AMS 5732, AMS 5734, AMS 5737, AMS 5804, AMS 5805, AMS 5853, AMS 5858, AMS 5895, AMS 7235, AMS 7477, AMS 7478, AMS 7479, AMS 7481, ASME 660, ASTM S66286, ASTM 660, AISI 660, AISI A286, SAE A286, SAE HEV-7, BS HR251, ASTM 665, GB/T 0Cr15Ni25Ti2MoAlVB, GB/T GH2132, GB/T GH2136, EN X6NiCrTiMoVB25-15-2, DIN 1.4943, DIN X4NiCrTi25-15, DIN X4NiCrTiMoV26-15, EN X4NiCrTiMoV26-15, EN 1.4943, DIN 1.4944, DIN X6NiCrTiMoV26-15, DIN 1.4944.4, AFNOR X6NiCrTiMoV26-15, BS X6NiCrTiMoV26-15, AISI S66286, SAE 660, SAE S66286, EN X6NiCrTiMoV26-15, EN 1.4944, UNS S66286, DIN 1.4980, DIN X5NiCrTi26-15, DIN X6NiCrTiMoVB25-15-2, AFNOR X6NiCrTiMoVB25-15-2, BS X6NiCrTiMoVB25-15-2, AISI HEV-7, JIS SUS616, EN 1.4980, ISO X6NiCrTiMoVB25-15-2, ISO 4606-661-86-X, ISO 4980-662-86-X, ISO PM42J, ASTM Grade 660
JIS G4311 Grade SUH660 ageing treatment after solution treatment general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.9 - 8.2 g/cm³ |
Typical for Austenitic Stainless Steel |
JIS G4311 Grade SUH660 ageing treatment after solution treatment thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K |
Typical for Austenitic Stainless Steel |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 440 J/(kg·K) |
Typical for Austenitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 11 - 21 W/(m·K) |
Typical for Austenitic Stainless Steel |
JIS G4311 Grade SUH660 ageing treatment after solution treatment electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
JIS G4311 Grade SUH660 ageing treatment after solution treatment mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 15 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 248 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 18 % |
- |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 990 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 590 MPa |
- |