UGI 4435 IRH Solution Annealed+Work Hardened(drawn)
UGI 4435 IRH Solution Annealed+Work Hardened(drawn) introduction
UGI 4435 IRH is an austenitic stainless steel (not magnetic) with a high Mo content and produced by a special method to optimize its cleanliness. Its composition provides it with very good corrosion resistance and is perfectly suited for prolonged contact with the skin. This grade also offers improved polishability, thanks to its inclusion population and its microstructure, adapted and controlled.
The chemical composition of UGI 4435 IRH is optimised to ensure primary ferritic solidification limiting hot workability problems and risks of crack formation at high temperature during welding, while providing it with a structure almost 100% austenitic at room temperature.
Grain size as per ASTM E-112: ≥ 5 (≥ 4 if need of guarantee of residual ferrite
Cleanliness as per DIN 50602, "M" method:
Sulphides (SS) + Oxides in Alignment (OA) + Silicates (OS): less than 4%
Dispersed or globular oxides (OG): less than 1%
Equivalent material: DIN 1.4435, ASTM 316L00109, JIS SUS316L, AISI 316 L00109, AFNOR X2CrNiMo18-14-3, EN 1.4435, BN2 1.4435, DIN X2CrNiMo18-14-3, EN X2CrNiMo18-14-3
UGI 4435 IRH Solution Annealed+Work Hardened(drawn) general
| Property |
Value |
| Density |
Density of 8 g/cm³ |
UGI 4435 IRH Solution Annealed+Work Hardened(drawn) thermal
| Property |
Value |
Comment |
| Coefficient of thermal expansion |
Coefficient of thermal expansion of 0.000016 1/K |
20 to 100°C |
| - |
Coefficient of thermal expansion of 0.0000165 1/K |
20 to 200°C |
| - |
Coefficient of thermal expansion of 0.000017 1/K |
20 to 300°C |
| - |
Coefficient of thermal expansion of 0.0000175 1/K |
20 to 400°C |
| - |
Coefficient of thermal expansion of 0.000018 1/K |
20 to 500°C |
| Specific heat capacity |
Specific heat capacity of 500 J/(kg·K) |
- |
| Thermal conductivity |
Thermal conductivity of 15 W/(m·K) |
- |
UGI 4435 IRH Solution Annealed+Work Hardened(drawn) chemical
| Property |
Value |
Comment |
| Carbon |
Carbon of 0.03 |
max. |
| Chromium |
Chromium of 17.0 - 19.0 % |
- |
| Manganese |
Manganese of 2.0 |
max. |
| Molybdenum |
Molybdenum of 2.5 - 3.0 % |
- |
| Nickel |
Nickel of 12.5 - 14.0 % |
- |
| Nitrogen |
Nitrogen of 0.11 |
max. |
| Phosphorus |
Phosphorus of 0.045 |
max. |
| Silicon |
Silicon of 1.0 |
max. |
| Sulfur |
Sulfur of 0.03 |
max. |
UGI 4435 IRH Solution Annealed+Work Hardened(drawn) electrical
| Property |
Value |
| Electrical resistivity |
Electrical resistivity of 7.500000000000001e-10 Ω·m |
UGI 4435 IRH Solution Annealed+Work Hardened(drawn) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20 °C |
Elastic modulus of 200 GPa |
- |
| - |
100 °C |
Elastic modulus of 194 GPa |
- |
| - |
200 °C |
Elastic modulus of 186 GPa |
- |
| - |
300 °C |
Elastic modulus of 180 GPa |
- |
| - |
400 °C |
Elastic modulus of 172 GPa |
- |
| - |
500 °C |
Elastic modulus of 165 GPa |
- |
| Elongation |
- |
Elongation of 25.0 - 30.0 % |
min., depending on the size |
| Tensile strength |
- |
Tensile strength of 500.0 - 950.0 MPa |
min., depending on the size |
UGI 4435 IRH Solution Annealed+Work Hardened(drawn) application
| Property |
- |
- |
| Application areas |
| Cold Forming |
| Corrosion properties |
| General machinability |
| Hot forming |
| Other |
Product |
Shape |
Finish |
Tolerance |
Dimensions (mm) |
| Rolled & descaled |
k13 |
Ø 13 to 130 |
| Turned |
10 + 11 |
Ø 22 to 130 |
| Ground |
7 + 8 + 9 + options |
Ø 2 to 130 |
| Drawn |
9 |
Ø 2 to 30 |
| Black bar |
+/- 1% of ø |
Ø 23 to 135 |
| Hexagonal |
Drawn |
10 + 11 |
Hex. 3 to 55 |
| Rolled |
- |
Ø 5 to 32 |
| Rolled & pickled |
- |
Ø 5 to 32 |
| Hexagonal |
Rolled & pickled |
- |
Hex. 12.4 to 28 |
| Billet |
Square |
As-rolled or as-heat-treated |
- |
50 to 120 |