SEW 410 Grade G-X5CrNiMo16-5 quenched and tempered (+QT)
SEW 410 Grade G-X5CrNiMo16-5 quenched and tempered (+QT) introduction
G-X 5 CrNiMo 16 5, for cast parts with increased strength, toughness and corrosion resistance, used for water turbines, pumps, armatures, compressors, ship propellers.
Equivalent material: DIN 1.4405, EN GX4CrNiMo16-5-1, EN 1.4405
SEW 410 Grade G-X5CrNiMo16-5 quenched and tempered (+QT) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.7 g/cm³ |
SEW 410 Grade G-X5CrNiMo16-5 quenched and tempered (+QT) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.1E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.2E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.25E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.3E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.35E-5 1/K |
- |
| Melting point |
- |
Melting point of 1370 - 1530 °C |
Typical for Martensitic Stainless Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 460 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 25 W/(m·K) |
- |
SEW 410 Grade G-X5CrNiMo16-5 quenched and tempered (+QT) chemical
| Property |
Value |
| Carbon |
Carbon of 0.07 % |
| Chromium |
Chromium of 15 - 16.5 % |
| Manganese |
Manganese of 1 % |
| Molybdenum |
Molybdenum of 0.5 - 2 % |
| Nickel |
Nickel of 4.5 - 6 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.025 % |
SEW 410 Grade G-X5CrNiMo16-5 quenched and tempered (+QT) electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 6E-7 Ω·m |
Typical for Martensitic Stainless Steel |
SEW 410 Grade G-X5CrNiMo16-5 quenched and tempered (+QT) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 220 GPa |
Typical for Martensitic Stainless Steel |
| Elongation |
20.0 °C |
Elongation of 15 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Martensitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Martensitic Stainless Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 760 - 960 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 540 MPa |
- |
| - |
100.0 °C |
Yield strength Rp0.2 of 515 MPa |
- |
| - |
200.0 °C |
Yield strength Rp0.2 of 485 MPa |
- |
| - |
300.0 °C |
Yield strength Rp0.2 of 455 MPa |
- |
Get the best value for your money with our top-grade steel at competitive prices.