EN 10213 Grade GX4CrNiMo16-5-1 quenched and tempered (+QT)
EN 10213 Grade GX4CrNiMo16-5-1 quenched and tempered (+QT) introduction
Material GX4CrNiMo16-5-1 is equivalent to trademark G-X 5 CrNiMo 16 5 acc. to SEW410-88. It is applicated at room temperature and increased temperatures. The DIN-make is used for castings with increased strength, ductility and corrosion properties for water turbines, pumps and fittings, compressors and ship propellers.
Equivalent material: DIN G-X5CrNiMo16-5, ISO G-X4CrNiMo16-5-1, DIN 1.4405, EN 1.4405
EN 10213 Grade GX4CrNiMo16-5-1 quenched and tempered (+QT) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.8 g/cm³ |
EN 10213 Grade GX4CrNiMo16-5-1 quenched and tempered (+QT) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.08E-5 - 1.1E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.2E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.15E-5 - 1.25E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.3E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.2E-5 - 1.35E-5 1/K |
- |
| Melting point |
- |
Melting point of 1370 - 1530 °C |
Typical for Martensitic Stainless Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 460 J/(kg·K) |
- |
| Thermal conductivity |
50.0 °C |
Thermal conductivity of 17 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 18 W/(m·K) |
- |
EN 10213 Grade GX4CrNiMo16-5-1 quenched and tempered (+QT) chemical
| Property |
Value |
| Carbon |
Carbon of 0.06 % |
| Chromium |
Chromium of 15 - 17 % |
| Copper |
Copper of 0.3 % |
| Manganese |
Manganese of 1 % |
| Molybdenum |
Molybdenum of 0.7 - 1.5 % |
| Nickel |
Nickel of 4 - 6 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 0.8 % |
| Sulfur |
Sulfur of 0.025 % |
| Vanadium |
Vanadium of 0.08 % |
EN 10213 Grade GX4CrNiMo16-5-1 quenched and tempered (+QT) electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 6E-7 Ω·m |
Typical for Martensitic Stainless Steel |
EN 10213 Grade GX4CrNiMo16-5-1 quenched and tempered (+QT) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 220 GPa |
Typical for Martensitic Stainless Steel |
| Elongation |
20.0 °C |
Elongation of 15 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Martensitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Martensitic Stainless Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 760 - 960 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 540 MPa |
- |
| - |
100.0 °C |
Yield strength Rp0.2 of 515 MPa |
- |
| - |
200.0 °C |
Yield strength Rp0.2 of 485 MPa |
- |
| - |
300.0 °C |
Yield strength Rp0.2 of 455 MPa |
- |
Our stringent quality control measures guarantee the highest standards of steel.
-- Our promise