Sandvik 6LR62 is a molybdenum-alloyed austenitic stainless steel.

Datasheet URL:
Sandvik 6LR62

Datasheet updated 2019-09-04 08:01 (supersedes all previous editions)

Equivalent material: UNS S31600, UNS S31609, ASTM TP316, ASTM TP316H, EN 1.4401, DIN 1.4401, AFNOR Z6ZND17-12, EN X5CrNiMo17-12-2

Sandvik 6LR62 general

Property Value Comment
Recycled Content Recycled Content of 82.1 % Average recycled content

Sandvik 6LR62 chemical

Property Value Comment
Carbon Carbon of 0.05 % min.
Chromium Chromium of 17 % -
Iron -
Manganese Manganese of 1.5 % -
Molybdenum Molybdenum of 2.1 % -
Nickel Nickel of 11.5 % -
Phosphorus Phosphorus of 0.04 % max.
Silicon Silicon of 0.6 % -
Sulfur Sulfur of 0.015 % max.

Sandvik 6LR62 electrical

Property - -
Welding

Sandvik 6LR62 mechanical

Property Temperature Value Comment
Creep strength 10^4 cycles 550.0 °C Creep strength 10^4 cycles of 255 MPa ISO values, at 10000h
- 575.0 °C Creep strength 10^4 cycles of 214 MPa ISO values, at 10000h
- 600.0 °C Creep strength 10^4 cycles of 172 MPa ISO values, at 10000h
- 625.0 °C Creep strength 10^4 cycles of 137 MPa ISO values, at 10000h
- 650.0 °C Creep strength 10^4 cycles of 108 MPa ISO values, at 10000h
- 675.0 °C Creep strength 10^4 cycles of 83 MPa ISO values, at 10000h
- 700.0 °C Creep strength 10^4 cycles of 64 MPa ISO values, at 10000h
- 725.0 °C Creep strength 10^4 cycles of 49 MPa ISO values, at 10000h
- 750.0 °C Creep strength 10^4 cycles of 37 MPa ISO values, at 10000h
Creep strength 10^5 cycles 550.0 °C Creep strength 10^5 cycles of 177 MPa ISO values, at 100000h
- 575.0 °C Creep strength 10^5 cycles of 137 MPa ISO values, at 100000h
- 600.0 °C Creep strength 10^5 cycles of 108 MPa ISO values, at 100000h
- 625.0 °C Creep strength 10^5 cycles of 86 MPa ISO values, at 100000h
- 650.0 °C Creep strength 10^5 cycles of 64 MPa ISO values, at 100000h
- 675.0 °C Creep strength 10^5 cycles of 46 MPa ISO values, at 100000h
- 700.0 °C Creep strength 10^5 cycles of 33 MPa ISO values, at 100000h
- 725.0 °C Creep strength 10^5 cycles of 25 MPa ISO values, at 100000h
- 750.0 °C Creep strength 10^5 cycles of 18 MPa ISO values, at 100000h
Elongation 23.0 °C Elongation of 45 % min.
Tensile strength 23.0 °C Tensile strength of 515 - 790 MPa -
Yield strength Rp0.2 20.0 °C Yield strength Rp0.2 of 205 MPa min.
- 50.0 °C Yield strength Rp0.2 of 196 MPa min.
- 100.0 °C Yield strength Rp0.2 of 175 MPa min.
- 150.0 °C Yield strength Rp0.2 of 158 MPa min.
- 200.0 °C Yield strength Rp0.2 of 145 MPa min.
- 250.0 °C Yield strength Rp0.2 of 135 MPa min.
- 300.0 °C Yield strength Rp0.2 of 127 MPa min.
- 350.0 °C Yield strength Rp0.2 of 120 MPa min.
- 400.0 °C Yield strength Rp0.2 of 115 MPa min.
- 450.0 °C Yield strength Rp0.2 of 112 MPa min.
- 500.0 °C Yield strength Rp0.2 of 110 MPa min.
- 550.0 °C Yield strength Rp0.2 of 108 MPa min.