ASTM A276 Grade 316 Relatively severe Cold work; Cold-Finished
Equivalent material: DIN 1.4401, DIN 316S42, DIN 316S33, DIN X5CrNiMo17-12-2, DIN X 5 CrNiMo 18 10, AFNOR Z7CND17-11-02, BS 316S16, UNI X5CrNiMo1712, SS 2347, UNE F.3543, AISI 316, SAE 316, JIS SUS316, JIS SUS316TKA, JIS SUS316TF, JIS SUS316FB, JIS SUSF316, JIS SUS316TKC, JIS SUS316TP, JIS SUS316TB, JIS SUS316TBS, JIS SUS316TPY, JIS SUS316TPD, JIS SUS316HTP, JIS SUS316HTB, JIS SUS316HTF, JIS SUS316F, EN X5CrNiMo17-12-2, EN 1.4401, ISO A4, GOST 0Cr17Ni12Mo2, GB 08Ch27N13M2, UNS S31600, IS X04Cr17Ni12Mo2, DIN 1.4984, AFNOR 9165-041, AFNOR 9165 25, AFNOR Z 10 CNW 17, EN 1.4984, ASTM F316, ASTM S31600, ASTM TP316, ASTM B8M, ASTM MT316
ASTM A276 Grade 316 Relatively severe Cold work; Cold-Finished general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.9 - 8.2 g/cm³ |
Typical for Austenitic Stainless Steel |
ASTM A276 Grade 316 Relatively severe Cold work; Cold-Finished thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K |
Typical for Austenitic Stainless Steel |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 440 J/(kg·K) |
Typical for Austenitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 11 - 21 W/(m·K) |
Typical for Austenitic Stainless Steel |
ASTM A276 Grade 316 Relatively severe Cold work; Cold-Finished chemical
| Property |
Value |
| Carbon |
Carbon of 0.08 % |
| Chromium |
Chromium of 16 - 18 % |
| Manganese |
Manganese of 2 % |
| Molybdenum |
Molybdenum of 2 - 3 % |
| Nickel |
Nickel of 10 - 14 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.03 % |
ASTM A276 Grade 316 Relatively severe Cold work; Cold-Finished electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
ASTM A276 Grade 316 Relatively severe Cold work; Cold-Finished mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 12 - 28 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 35 - 45 % |
- |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 655 - 860 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 310 - 690 MPa |
- |