Sandvik 2RE10 introduction

Sandvik 2RE10 is an austenitic stainless steel with extremely low carbon and impurity contents. The grade is characterized by:

Excellent resistance to corrosion in nitric acid
Excellent resistance to intergranular corrosion
Good resistance to pitting
Good weldability

Sandvik 2RE10 conforms to EN no. 1.4335, but actual composition specified for EN no. 1.4335 allows considerable higher maximum levels of C, Si, P, S and Mo. High levels of these elements increase the potential for corrosion and have therefore been kept as low as possible in Sandvik 2RE10.

More technical information and charts that are relevant to the materials corrosion, mechanical and physical performance are displayed in the figures on the right side of the material page.

Datasheet URL:
Sandvik 2RE10

Datasheet updated 2019-08-16 15:04 (supersedes all previous editions)

Equivalent material: UNS S31002, EN 1.4335, DIN 1.4335, DIN X1CrNi25-21, EN X1CrNi25-21

Sandvik 2RE10 general

Property Temperature Value Comment
Density 23.0 °C Density of 7.9 g/cm³ -
Recycled Content - Recycled Content of 82.1 % Average recycled content

Sandvik 2RE10 thermal

Property Temperature Value Comment
Coefficient of thermal expansion 100.0 °C Coefficient of thermal expansion of 1.55E-5 1/K for 30°C to the mentioned temperature
- 200.0 °C Coefficient of thermal expansion of 1.65E-5 1/K for 30°C to the mentioned temperature
- 300.0 °C Coefficient of thermal expansion of 1.7E-5 1/K for 30°C to the mentioned temperature
- 400.0 °C Coefficient of thermal expansion of 1.7E-5 1/K for 30°C to the mentioned temperature
- 500.0 °C Coefficient of thermal expansion of 1.75E-5 1/K for 30°C to the mentioned temperature
- 600.0 °C Coefficient of thermal expansion of 1.75E-5 1/K for 30°C to the mentioned temperature
- 700.0 °C Coefficient of thermal expansion of 1.8E-5 1/K for 30°C to the mentioned temperature
Specific heat capacity 20.0 °C Specific heat capacity of 470 J/(kg·K) -
- 100.0 °C Specific heat capacity of 495 J/(kg·K) -
- 200.0 °C Specific heat capacity of 530 J/(kg·K) -
- 300.0 °C Specific heat capacity of 555 J/(kg·K) -
- 400.0 °C Specific heat capacity of 580 J/(kg·K) -
- 500.0 °C Specific heat capacity of 600 J/(kg·K) -
- 600.0 °C Specific heat capacity of 615 J/(kg·K) -
- 700.0 °C Specific heat capacity of 630 J/(kg·K) -
Thermal conductivity 20.0 °C Thermal conductivity of 13 W/(m·K) -
- 100.0 °C Thermal conductivity of 15 W/(m·K) -
- 200.0 °C Thermal conductivity of 17 W/(m·K) -
- 300.0 °C Thermal conductivity of 19 W/(m·K) -
- 400.0 °C Thermal conductivity of 21 W/(m·K) -
- 500.0 °C Thermal conductivity of 23 W/(m·K) -
- 600.0 °C Thermal conductivity of 25 W/(m·K) -
- 700.0 °C Thermal conductivity of 26 W/(m·K) -

Sandvik 2RE10 chemical

Property Value Comment
Carbon Carbon of 0.015 % max.
Chromium Chromium of 24.5 % -
Iron -
Manganese Manganese of 1.8 % -
Molybdenum Molybdenum of 0.1 % -
Nickel Nickel of 20 % -
Phosphorus Phosphorus of 0.02 % max.
Silicon Silicon of 0.15 % max.
Sulfur Sulfur of 5E-3 % max.

Sandvik 2RE10 electrical

Property Temperature Value
Electrical resistivity 20.0 °C Electrical resistivity of 8.4E-7 Ω·m
- 100.0 °C Electrical resistivity of 9E-7 Ω·m
- 200.0 °C Electrical resistivity of 9.8E-7 Ω·m
- 300.0 °C Electrical resistivity of 1.07E-6 Ω·m
- 400.0 °C Electrical resistivity of 1.1E-6 Ω·m
- 500.0 °C Electrical resistivity of 1.14E-6 Ω·m
- 600.0 °C Electrical resistivity of 1.18E-6 Ω·m
- 700.0 °C Electrical resistivity of 1.2E-6 Ω·m
- 800.0 °C Electrical resistivity of 1.22E-6 Ω·m
- 900.0 °C Electrical resistivity of 1.23E-6 Ω·m
- 1000.0 °C Electrical resistivity of 1.24E-6 Ω·m

Sandvik 2RE10 mechanical

Property Temperature Value Comment
Charpy impact energy -270.0 °C Charpy impact energy of 60 J min., EN 13445-2 (UFPV-2) and EN 10216-5
- -196.0 °C Charpy impact energy of 60 J min., EN 13445-2 (UFPV-2) and EN 10216-5
Elastic modulus 20.0 °C Elastic modulus of 195 GPa -
- 100.0 °C Elastic modulus of 190 GPa -
- 200.0 °C Elastic modulus of 182 GPa -
- 300.0 °C Elastic modulus of 174 GPa -
- 400.0 °C Elastic modulus of 166 GPa -
- 500.0 °C Elastic modulus of 158 GPa -
Elongation 23.0 °C Elongation of 35 % min.
Hardness, Vickers 23.0 °C Hardness, Vickers of 155 [-] -
Tensile strength 20.0 °C Tensile strength of 500 - 670 MPa -
- 50.0 °C Tensile strength of 485 MPa -
- 100.0 °C Tensile strength of 470 MPa -
- 150.0 °C Tensile strength of 455 MPa -
- 200.0 °C Tensile strength of 440 MPa -
- 250.0 °C Tensile strength of 430 MPa -
- 300.0 °C Tensile strength of 420 MPa -
- 350.0 °C Tensile strength of 415 MPa -
- 400.0 °C Tensile strength of 410 MPa -
Yield strength Rp0.1 20.0 °C Yield strength Rp0.1 of 210 MPa min.
- 50.0 °C Yield strength Rp0.1 of 225 MPa min.
- 100.0 °C Yield strength Rp0.1 of 210 MPa min.
- 150.0 °C Yield strength Rp0.1 of 200 MPa min.
- 200.0 °C Yield strength Rp0.1 of 190 MPa min.
- 250.0 °C Yield strength Rp0.1 of 180 MPa min.
- 300.0 °C Yield strength Rp0.1 of 170 MPa min.
- 350.0 °C Yield strength Rp0.1 of 165 MPa min.
- 400.0 °C Yield strength Rp0.1 of 160 MPa min.
Yield strength Rp0.2 20.0 °C Yield strength Rp0.2 of 205 MPa min.
- 50.0 °C Yield strength Rp0.2 of 195 MPa min.
- 100.0 °C Yield strength Rp0.2 of 180 MPa min.
- 150.0 °C Yield strength Rp0.2 of 170 MPa min.
- 200.0 °C Yield strength Rp0.2 of 160 MPa min.
- 250.0 °C Yield strength Rp0.2 of 150 MPa min.
- 300.0 °C Yield strength Rp0.2 of 145 MPa min.
- 350.0 °C Yield strength Rp0.2 of 140 MPa min.
- 400.0 °C Yield strength Rp0.2 of 135 MPa min.

Sandvik 2RE10 application

Property - -
Application areas
Certifications
Cold Forming
Corrosion properties
Heat Treatment
Other
Welding