SAE J405 Grade S32760
Equivalent material: DIN 1.4501, DIN 25-7-4, DIN S32760, DIN X2CrNiMoCuWN25-7-4, AFNOR Z3CNDUW25-07Az, BS X2CrNiMoCuWN25-7-4, AISI S32760, JIS SM25Cr, EN X2CrNiMoCuWN25-7-4, EN 1.4501, ISO X2CrNiMoCuWN25-7-4, ISO 4501-327-60-I, ISO DM36B, ISO 56, GB 022Cr25Ni7Mo3WCuN, ASTM Type F 55, ASTM Grade F55, UNS S32760
SAE J405 Grade S32760 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
Typical for Duplex Stainless Steel |
SAE J405 Grade S32760 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1E-5 1/K |
Typical for Duplex Stainless Steel |
| Max service temperature |
- |
Max service temperature of 300 °C |
Typical for Duplex Stainless Steel |
| Melting point |
- |
Melting point of 1375 - 1450 °C |
Typical for Duplex Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 440 - 502 J/(kg·K) |
Typical for Duplex Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 13 - 30 W/(m·K) |
Typical for Duplex Stainless Steel |
SAE J405 Grade S32760 chemical
| Property |
Value |
| Carbon |
Carbon of 0.03 % |
| Chromium |
Chromium of 24 - 26 % |
| Copper |
Copper of 0.5 - 1 % |
| Manganese |
Manganese of 1 % |
| Molybdenum |
Molybdenum of 3 - 4 % |
| Nickel |
Nickel of 6 - 8 % |
| Nitrogen |
Nitrogen of 0.2 - 0.3 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.01 % |
| Tungsten |
Tungsten of 0.5 - 1 % |
SAE J405 Grade S32760 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 GPa |
Typical for Duplex Stainless Steel |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Duplex Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Duplex Stainless Steel |
We offer top-notch steel without compromising on quality or affordability.
-- Our promise
Similar or equivalent steel materials