EN 10272 Grade X2CrNiMoCuWN25-7-4 solution annealed (+AT)
EN 10272 Grade X2CrNiMoCuWN25-7-4 solution annealed (+AT) introduction
The austenitic-ferritic material X2CrNiMoCuWN25-7-4 is applicated in solution annealed condition in the form of warm rolled sheet, rods, wire rods and profiles. The material is resistant to intercrystalline corrosion also in sensitized condition.
Equivalent material: ASTM S32760, UNS S32760, GB 022Cr25Ni7Mo4WCuN, GB S27603, ASTM A479UNSS32760, DIN 1.4501, DIN 25-7-4, DIN S32760, DIN X2CrNiMoCuWN25-7-4, AFNOR Z3CNDUW25-07Az, BS X2CrNiMoCuWN25-7-4, AISI S32760, SAE S32760, JIS SM25Cr, EN 1.4501, ISO X2CrNiMoCuWN25-7-4, ISO 4501-327-60-I, ISO DM36B, ISO 56, GB 022Cr25Ni7Mo3WCuN, ASTM Type F 55, ASTM Grade F55
EN 10272 Grade X2CrNiMoCuWN25-7-4 solution annealed (+AT) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.8 g/cm³ |
EN 10272 Grade X2CrNiMoCuWN25-7-4 solution annealed (+AT) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.3E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.35E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.4E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 300 °C |
Typical for Duplex Stainless Steel |
| Melting point |
- |
Melting point of 1375 - 1450 °C |
Typical for Duplex Stainless Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 500 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 15 W/(m·K) |
- |
EN 10272 Grade X2CrNiMoCuWN25-7-4 solution annealed (+AT) chemical
| Property |
Value |
| Carbon |
Carbon of 0.03 % |
| Chromium |
Chromium of 24 - 26 % |
| Copper |
Copper of 0.5 - 1 % |
| Manganese |
Manganese of 1 % |
| Molybdenum |
Molybdenum of 3 - 4 % |
| Nickel |
Nickel of 6 - 8 % |
| Nitrogen |
Nitrogen of 0.2 - 0.3 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.015 % |
| Tungsten |
Tungsten of 0.5 - 1 % |
EN 10272 Grade X2CrNiMoCuWN25-7-4 solution annealed (+AT) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 8E-7 Ω·m |
EN 10272 Grade X2CrNiMoCuWN25-7-4 solution annealed (+AT) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 200 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 194 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 186 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 180 GPa |
- |
| Elongation |
20.0 °C |
Elongation of 25 % |
- |
| Hardness, Brinell |
20.0 °C |
Hardness, Brinell of 290 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Duplex Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Duplex Stainless Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 730 - 930 MPa |
- |
| - |
100.0 °C |
Tensile strength of 680 MPa |
- |
| - |
150.0 °C |
Tensile strength of 660 MPa |
- |
| - |
200.0 °C |
Tensile strength of 640 MPa |
- |
| - |
250.0 °C |
Tensile strength of 630 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 530 MPa |
- |
| - |
100.0 °C |
Yield strength Rp0.2 of 450 MPa |
- |
| - |
150.0 °C |
Yield strength Rp0.2 of 420 MPa |
- |
| - |
200.0 °C |
Yield strength Rp0.2 of 400 MPa |
- |
| - |
250.0 °C |
Yield strength Rp0.2 of 380 MPa |
- |